In situ nanocompression testing of irradiated copper
Source abstract
Abstract
Increasing demand for energy and reduction of carbon dioxide emissions has revived interest in nuclear energy. Designing materials for radiation environments necessitates a fundamental understanding of how radiation-induced defects alter mechanical properties. Ion beams create radiation damage efficiently without material activation, but their limited penetration depth requires small-scale testing. However, strength measurements of nanoscale irradiated specimens have not been previously performed. Here we show that yield strengths approaching macroscopic values are measured from irradiated ~400 nm-diameter copper specimens. Quantitative in situ nanocompression testing in a transmission electron microscope reveals that the strength of larger samples is controlled by dislocation-irradiation defect interactions, yielding size-independent strengths. Below ~400 nm, size-dependent strength results from dislocation source limitation. This transition length-scale should be universal, but depends on material and irradiation conditions. We conclude that for irradiated copper, and presumably related materials, nanoscale in situ testing can determine bulk-like yield strengths and simultaneously identify deformation mechanisms.
Source: europepmc · Quality: candidate unverified · Source record ↗
Research context
OpenAlex topics: Microstructure and mechanical properties · Fusion materials and technologies · Ion-surface interactions and analysis
SciVX discovery tags are terminology-based. OpenAlex topics are source-provided classifications.
References (36)
Show source-provided references
1. Grimes, R. W. & Nuttall, W. J. Generating the option of a two-stage nuclear renaissance. Science 329, 799–803 (2010).10.1126/science.1188928 ↗
2. Odette, G. R., Alinger, M. J. & Wirth, B. D. Recent developments in irradiation-resistant steels. Annu. Rev. Mater. Res. 38, 471–503 (2008).10.1146/annurev.matsci.38.060407.130315 ↗
3. Greenfield, I. & Wilsdorf, H. G. Effect of neutron irradiation on plastic deformation of copper single crystals. J. Appl. Phys. 32, 827–839 (1961).10.1063/1.1736114 ↗
4. Bei, H., Shim, S., Miller, M. K., Pharr, G. M. & George, E. P. Effects of focused ion beam milling on the nanomechanical behaviour of a molybdenum-alloy single crystal. Appl. Phys. Lett. 91, 111915 (2007).10.1063/1.2784948 ↗
5. Mansur, L. K. Theory and experimental background on dimensional changes in irradiated alloys. J. Nucl. Mater. 216, 97–123 (1994).10.1016/0022-3115(94)90009-4 ↗
6. Was, G. S. et al. Emulation of neutron irradiation effects with protons: Validation of principle. J. Nucl. Mater. 300, 198–216 (2002).10.1016/S0022-3115(01)00751-6 ↗
7. Oliver, W. C. & Pharr, G. M. An improved technique for determining hardness and elastic modulus using load and displacement sensing indentation experiments. J. Mater. Res. 7, 1564–1583 (1992).10.1557/JMR.1992.1564 ↗
8. Pharr, G. M., Herbert, E. G. & Gao, Y. The indentation size effect: A critical examination of experimental observations and mechanistic interpretations. Annu. Rev. Mater. Res. 40, 271–292 (2010).10.1146/annurev-matsci-070909-104456 ↗
9. Hosemann, P. et al. An exploratory study to determine applicability of nano-hardness and micro-compression measurements for yield stress estimation. J. Nucl. Mater. 375, 135–143 (2008).10.1016/j.jnucmat.2007.11.004 ↗
10. Kiener, D., Durst, K., Rester, M. & Minor, A. M. Revealing deformation mechanisms with nanoindentation. JOM 61, 14–23 (2009).10.1007/s11837-009-0036-4 ↗
11. Uchic, M. D., Dimiduk, D. M., Florando, J. N. & Nix, W. D. Sample dimensions influence strength and crystal plasticity. Science 305, 986–989 (2004).10.1126/science.1098993 ↗
12. Uchic, M. D., Shade, P. A. & Dimiduk, D. Plasticity of micrometer-scale single crystals in compression. Annu. Rev. Mater. Res. 39, 361–386 (2009).10.1146/annurev-matsci-082908-145422 ↗
13. Li, N., Mara, N. A., Wang, Y. Q., Nastasi, M. & Misra, A. Compressive flow behaviour of Cu thin films and Cu/Nb multilayers containing nanometer-scale helium bubbles. Scr. Mater. 64, 974–977 (2011).10.1016/j.scriptamat.2011.02.001 ↗
14. Shan, Z. W., Mishra, R. K., Asif, S. A. S., Warren, O. L. & Minor, A. M. Mechanical annealing and source-limited deformation in submicrometre-diameter Ni crystals. Nature Mater. 73, 115–119 (2008).10.1038/nmat2085 ↗
15. Oh, S. H., Legros, M., Kiener, D. & Dehm, G. In situ observation of dislocation nucleation and escape in a submicron Al single-crystal. Nature Mater. 8, 95–100 (2009).10.1038/nmat2370 ↗
16. Jang, D. C. & Greer, J. R. Transition from a strong-yet-brittle to a stronger-and-ductile state by size reduction of metallic glasses. Nature Mater. 9, 215–219 (2010).10.1038/nmat2622 ↗
17. Gianola, D. S. & Eberl, C. Micro- and nanoscale tensile testing of materials. JOM 61, 24–35 (2009).10.1007/s11837-009-0037-3 ↗
18. Yu, Q. et al. Strong crystal size effect on deformation twinning. Nature 463, 335–338 (2010).10.1038/nature08692 ↗
19. Marian, J., Martinez, E., Lee, H. J. & Wirth, B. D. Micro/meso-scale computational study of dislocation-stacking-fault tetrahedron interactions in copper. J. Mater. Res. 24, 3628–3635 (2009).10.1557/jmr.2009.0424 ↗
20. Kadoyoshi, T. et al. Molecular dynamics study on the formation of stacking fault tetrahedra and unfaulting of Frank loops in fcc metals. Acta Mater. 55, 3073–3080 (2007).10.1016/j.actamat.2007.01.010 ↗
21. Bacon, D. J., Gao, F. & Osetsky, Y. N. The primary damage state in fcc, bcc and hcp metals as seen in molecular dynamics simulations. J. Nucl. Mater. 276, 1–12 (2000).10.1016/S0022-3115(99)00165-8 ↗
22. Robach, J. S., Robertson, I. M., Lee, H. J. & Wirth, B. D. Dynamic observations and atomistic simulations of dislocation-defect interactions in rapidly quenched copper and gold. Acta Mater. 54, 1679–1690 (2006).10.1016/j.actamat.2005.11.038 ↗
23. Matsukawa, Y., Briceno, M. & Robertson, I. M. Combining in situ transmission electron microscopy and molecular dynamics computer simulations to reveal the interaction mechanisms of dislocations with stacking-fault tetrahedron in nuclear materials. Microsc. Res. Tech. 72, 284–292 (2009).10.1002/jemt.20681 ↗
24. Matsukawa, Y., Osetsky, Y. N., Stoller, R. E. & Zinkle, S. J. Destruction processes of large stacking fault tetrahedra induced by direct interaction with gliding dislocations. J. Nucl. Mater. 351, 285–294 (2006).10.1016/j.jnucmat.2006.02.003 ↗
25. Minor, A. M., Morris, J. W. & Stach, E. A. Quantitative in situ nanoindentation in an electron microscope. Appl. Phys. Lett. 79, 1625–1627 (2001).10.1063/1.1400768 ↗
26. Minor, A. M. et al. A new view of the onset of plasticity during the nanoindentation of aluminium. Nature Mater. 5, 697–702 (2006).10.1038/nmat1714 ↗
27. Greer, J. R. Bridging the gap between computational and experimental length scales: A review on nanoscale plasticity. Rev. Adv. Mater. Sci. 13, 59–70 (2006).
28. Kiener, D. & Minor, A. M. Source controlled yield and hardening of Cu(100) studied by in situ transmission electron microscopy. Acta Mater. 59, 1328–1337 (2011).10.1016/j.actamat.2010.10.065 ↗
29. Dai, Y. & Victoria, M. Defect structures in deformed FCC metals. Acta Mater. 45, 3495–3501 (1997).10.1016/S1359-6454(97)00019-0 ↗
30. Singh, B. N. & Zinkle, S. J. Defect accumulation in pure fcc metals in the transient regime: A review. J. Nucl. Mater. 206, 212–229 (1993).10.1016/0022-3115(93)90125-I ↗
31. Arzt, E. Size effects in materials due to microstructural and dimensional constraints: A comparative review. Acta Mater. 46, 5611–5626 (1998).10.1016/S1359-6454(98)00231-6 ↗
32. Girault, B., Schneider, A. S., Frick, C. P. & Arzt, E. Strength effects in micropillars of a dispersion strengthened superalloy. Adv. Eng. Mater. 12, 385–388 (2010).10.1002/adem.201000089 ↗
33. Rao, S. I. et al. Estimating the strength of single-ended dislocation sources in micron-sized single crystals. Phil. Mag. 87, 4777–4794 (2007).10.1080/14786430701591513 ↗
34. Singh, B. N., Horsewell, A., Toft, P. & Edwards, D. J. Temperature and dose dependencies of microstructure and hardness of neutron irradiated OFHC copper. J. Nucl. Mater. 224, 131–140 (1995).10.1016/0022-3115(95)00054-2 ↗
35. Ziegler, J. F., Biersack, J. P. & Littmark, U. The Stopping Range of Ions in Matter (Pergamon, 1985).10.1007/978-1-4615-8103-1_3 ↗
36. Hosemann, P., Maloy, S. A., Greco, R. R., Swadener, J. G. & Romero, T. Oxygen effects on irradiated tantalum alloys. J. Nucl. Mater. 384, 25–29 (2009).10.1016/j.jnucmat.2008.09.027 ↗