Gradient Li-rich oxide cathode particles immunized against oxygen release by a molten salt treatment

Zhi Zhu, Daiwei Yu, Yang Yang, Cong Su, Yimeng Huang, Yanhao Dong, Iradwikanari Waluyo, Baoming Wang, Adrian Hunt, Xiahui Yao, Jinhyuk Lee, Weijiang Xue, Ju Li

Nature Energy· Volume 4· Issue 12

Abstract

Lithium-rich transition metal oxide (Li1+XM1−XO2) cathodes have high energy density above 900 Wh kg−1 due to hybrid anion- and cation-redox (HACR) contributions, but critical issues such as oxygen release and voltage decay during cycling have prevented their application for years. Here we show that a molten molybdate-assisted LiO extraction at 700 °C creates lattice-coherent but depth (r)-dependent Li1+X(r)M1−X(r)O2 particles with a Li-rich (X ≈ 0.2) interior, a Li-poor (X ≈ −0.05) surface and a continuous gradient in between. The gradient Li-rich single crystals eliminate the oxygen release to the electrolyte and, importantly, still allow stable oxygen redox contributions within. Both the metal valence states and the crystal structure are well maintained during cycling. The gradient HACR cathode displays a specific density of 843 Wh kg−1 after 200 cycles at 0.2C and 808 Wh kg−1 after 100 cycles at 1C, with very little oxygen release and consumption of electrolyte. This high-temperature immunization treatment can be generalized to leach other elements to avoid unexpected surface reactions in batteries. Critical issues such as oxygen release during battery cycling plague the development of high-energy Li-rich oxide cathodes. Here the authors report a Li-gradient structure of the oxides, obtained by a selective LiO leaching process via a molten salt treatment, displaying virtually zero oxygen loss.
Source: openaire · Quality: candidate unverified · Source record ↗

Research context

OpenAlex topics: Advancements in Battery Materials · Advanced Battery Materials and Technologies · Supercapacitor Materials and Fabrication

SciVX discovery tags are terminology-based. OpenAlex topics are source-provided classifications.

References (46)

Show source-provided references
1. Xue, W. et al. Intercalation-conversion hybrid cathodes enabling Li–S full-cell architectures with jointly superior gravimetric and volumetric energy densities. Nat. Energy 4, 374–382 (2019).10.1038/s41560-019-0351-0 ↗
2. Zhu, Z. et al. Anion-redox nanolithia cathodes for Li-ion batteries. Nat. Energy 1, 16111 (2016).10.1038/nenergy.2016.111 ↗
3. Qiao, Y., Jiang, K. Z., Deng, H. & Zhou, H. S. A high-energy-density and long-life lithium-ion battery via reversible oxide–peroxide conversion. Nat. Catal. 2, 1035–1044 (2019).10.1038/s41929-019-0362-z ↗
4. Kim, S., Cho, W., Zhang, X., Oshima, Y. & Choi, J. W. A stable lithium-rich surface structure for lithium-rich layered cathode materials. Nat. Commun. 7, 13598 (2016).
5. Luo, K. et al. One-pot synthesis of lithium-rich cathode material with hierarchical morphology. Nano Lett. 16, 7503–7508 (2016).10.1021/acs.nanolett.6b03296 ↗
6. Yu, H. J. & Zhou, H. S. High-energy cathode materials (Li2MnO3–LiMO2) for lithium-ion batteries. J. Phys. Chem. Lett. 4, 1268–1280 (2013).10.1021/jz400032v ↗
7. Yu, H. J. et al. High-energy ‘composite’ layered manganese-rich cathode materials via controlling Li2MnO3 phase activation for lithium-ion batteries. Phys. Chem. Chem. Phys. 14, 6584–6595 (2012).10.1039/c2cp40745k ↗
8. Ye, D. L. et al. Understanding the origin of Li2MnO3 activation in Li-rich cathode materials for lithium-ion batteries. Adv. Fun. Mater. 25, 7488–7496 (2015).10.1002/adfm.201503276 ↗
9. Seo, D.-H. et al. The structural and chemical origin of the oxygen redox activity in layered and cation-disordered Li-excess cathode materials. Nat. Chem. 8, 692–697 (2016).10.1038/nchem.2524 ↗
10. Yan, P. et al. Injection of oxygen vacancies in the bulk lattice of layered cathodes. Nat. Nanotechnol. 14, 602–608 (2019).10.1038/s41565-019-0428-8 ↗
11. Lee, E. & Persson, K. A. Structural and chemical evolution of the layered Li-excess LixMnO3 as a function of Li content from first-principles calculations. Adv. Energy Mater. 4, 1400498 (2014).10.1002/aenm.201400498 ↗
12. Luo, K. et al. Charge-compensation in 3d-transition-metal-oxide intercalation cathodes through the generation of localized electron holes on oxygen. Nat. Chem. 8, 684–691 (2016).10.1038/nchem.2471 ↗
13. Lee, J. Y. et al. Mitigating oxygen loss to improve the cycling performance of high capacity cation-disordered cathode materials. Nat. Commun. 8, 981 (2017).
14. Chen, H. R. & Islam, M. S. Lithium extraction mechanism in Li-rich Li2MnO3 involving oxygen hole formation and dimerization. Chem. Mater. 28, 6656–6663 (2016).10.1021/acs.chemmater.6b02870 ↗
15. Singer, A. et al. Nucleation of dislocations and their dynamics in layered oxide cathode materials during battery charging. Nat. Energy 3, 641–647 (2018).10.1038/s41560-018-0184-2 ↗
16. Hu, E. Y. et al. Evolution of redox couples in Li- and Mn-rich cathode materials and mitigation of voltage fade by reducing oxygen release. Nat. Energy 3, 690–698 (2018).10.1038/s41560-018-0207-z ↗
17. Hy, S., Felix, F., Rick, J., Su, W. N. & Hwang, B. J. Direct in situ observation of Li2O evolution on Li-rich high-capacity cathode material, Li[NixLi(1−2x)/3Mn(2−x)/3]O2 (0 ≤ x ≤0.5). J. Am. Chem. Soc. 136, 999–1007 (2014).10.1021/ja410137s ↗
18. Tran, N. et al. Mechanisms associated with the “plateau” observed at high voltage for the overlithiated Li1.12(Ni0.425Mn0.425Co0.15)0.88O2 system. Chem. Mater. 20, 4815–4825 (2008).10.1021/cm070435m ↗
19. Yan, P. F. et al. Probing the degradation mechanism of Li2MnO3 cathode for Li-ion batteries. Chem. Mater. 27, 975–982 (2015).10.1021/cm504257m ↗
20. Guo, S. H. et al. Surface coating of lithium-manganese-rich layered oxides with delaminated MnO2 nanosheets as cathode materials for Li-ion batteries. J. Mater. Chem. A 2, 4422–4428 (2014).10.1039/c3ta15206e ↗
21. Zheng, F. H. et al. Nanoscale surface modification of lithium-rich layered-oxide composite cathodes for suppressing voltage fade. Angew. Chem. Int. Ed. 54, 13058–13062 (2015).10.1002/anie.201506408 ↗
22. Kang, S. H., Johnson, C. S., Vaughey, J. T., Amine, K. & Thackeray, M. M. The effects of acid treatment on the electrochemical properties of 0.5 Li2MnO3 ∙ 0.5 LiNi0.44Co0.25Mn0.31O2 electrodes in lithium cells. J. Electrochem. Soc. 153, A1186–A1192 (2006).10.1149/1.2194764 ↗
23. Qiu, B. et al. Gas–solid interfacial modification of oxygen activity in layered oxide cathodes for lithium-ion batteries. Nat. Commun. 7, 12108 (2016).
24. Bruce, P. G., Freunberger, S. A., Hardwick, L. J. & Tarascon, J. M. Li–O2 and Li–S batteries with high energy storage. Nat. Mater. 11, 19–29 (2012).10.1038/nmat3191 ↗
25. Freunberger, S. A. et al. Reactions in the rechargeable lithium–O2 battery with alkyl carbonate electrolytes. J. Am. Chem. Soc. 133, 8040–8047 (2011).10.1021/ja2021747 ↗
26. McCloskey, B. D., Bethune, D. S., Shelby, R. M., Girishkumar, G. & Luntz, A. C. Solvents’ critical role in nonaqueous lithium–oxygen battery electrochemistry. J. Phys. Chem. Lett. 2, 1161–1166 (2011).10.1021/jz200352v ↗
27. Sun, Y.-K. et al. Nanostructured high-energy cathode materials for advanced lithium batteries. Nat. Mater. 11, 942–947 (2012).10.1038/nmat3435 ↗
28. Lim, B. B. et al. Advanced concentration gradient cathode material with two-slope for high-energy and safe lithium batteries. Adv. Funct. Mater. 25, 4673–4680 (2015).10.1002/adfm.201501430 ↗
29. Nakamura, T. et al. Defect chemical studies on oxygen release from the Li-rich cathode material Li1.2Mn0.6Ni0.2O2−δ. J. Mater. Chem. A 7, 5009–5019 (2019).10.1039/C8TA12484A ↗
30. Cho, Y., Oh, P. & Cho, J. A new type of protective surface layer for high-capacity Ni-based cathode materials: nanoscaled surface pillaring layer. Nano Lett. 13, 1145–1152 (2013).10.1021/nl304558t ↗
31. Loomer, D. B., Al, T. A., Weaver, L. & Cogswell, S. Manganese valence imaging in Mn minerals at the nanoscale using STEM-EELS. Am. Mineral. 92, 72–79 (2007).10.2138/am.2007.2252 ↗
32. Li, Z. P. et al. Interface and surface cation stoichiometry modified by oxygen vacancies in epitaxial manganite films. Adv. Funct. Mater. 22, 4312–4321 (2012).10.1002/adfm.201200143 ↗
33. Lu, J. et al. Nanoscale coating of LiMO2 (M = Ni, Co, Mn) nanobelts with Li+-conductive Li2TiO3: toward better rate capabilities for Li-ion batteries. J. Am. Chem. Soc. 135, 1649–1652 (2013).10.1021/ja308717z ↗
34. Qiao, R. et al. Direct experimental probe of the Ni(II)/Ni(III)/Ni(IV) redox evolution in LiNi0.5Mn1.5O4 electrodes. J. Phys. Chem. C. 119, 27228–27233 (2015).10.1021/acs.jpcc.5b07479 ↗
35. Luo, K. et al. Anion redox chemistry in the cobalt free 3d transition metal oxide intercalation electrode Li[Li0.2Ni0.2Mn0.6]O2. J. Am. Chem. Soc. 138, 11211–11218 (2016).10.1021/jacs.6b05111 ↗
36. Oishi, M. et al. Direct observation of reversible oxygen anion redox reaction in Li-rich manganese oxide, Li2MnO3, studied by soft X-ray absorption spectroscopy. J. Mater. Chem. A 4, 9293–9302 (2016).10.1039/C6TA00174B ↗
37. Dai, K. H. et al. High reversibility of lattice oxygen redox quantified by direct bulk probes of both anionic and cationic redox reactions. Joule 3, 518–541 (2019).10.1016/j.joule.2018.11.014 ↗
38. Qiao, R. M. et al. Direct evidence of gradient Mn(II) evolution at charged states in LiNi0.5Mn1.5O4 electrodes with capacity fading. J. Power Sources 273, 1120–1126 (2015).10.1016/j.jpowsour.2014.10.013 ↗
39. Risch, M. et al. Redox processes of manganese oxide in catalyzing oxygen evolution and reduction: an in situ soft X-ray absorption spectroscopy study. J. Phys. Chem. C. 121, 17682–17692 (2017).10.1021/acs.jpcc.7b05592 ↗
40. Li, Q. H. et al. Quantitative probe of the transition metal redox in battery electrodes through soft X-ray absorption spectroscopy. J. Phys. D. 49, 413003 (2016).10.1088/0022-3727/49/41/413003 ↗
41. Venkatraman, S., Shin, Y. & Manthiram, A. Phase relationships and structural and chemical stabilities of charged Li1 − xCoO2 − δ and Li1 − xNi0.85Co0.15O2 − δ cathodes. Electrochem. Solid State Lett. 6, A9–A12 (2003).10.1149/1.1525430 ↗
42. Hatsukade, T., Schiele, A., Hartmann, P., Brezesinski, T. & Janek, J. Origin of carbon dioxide evolved during cycling of nickel-rich layered NCM cathodes. ACS Appl. Mater. Interfaces 10, 38892–38899 (2018).10.1021/acsami.8b13158 ↗
43. Imhof, R. & Novak, P. Oxidative electrolyte solvent degradation in lithium-ion batteries: an in situ differential electrochemical mass spectrometry investigation. J. Electrochem. Soc. 146, 1702–1706 (1999).10.1149/1.1391829 ↗
44. Jung, R., Metzger, M., Maglia, F., Stinner, C. & Gasteiger, H. A. Oxygen release and its effect on the cycling stability of LiNixMnyCozO2 (NMC) cathode materials for Li-ion batteries. J. Electrochem. Soc. 164, A1361–A1377 (2017).10.1149/2.0021707jes ↗
45. Wang, H. et al. CO2 and O2 evolution at high voltage cathode materials of Li-ion batteries: a differential electrochemical mass spectrometry study. Anal. Chem. 86, 6197–6201 (2014).10.1021/ac403317d ↗
46. de Biasi, L. et al. Chemical, structural, and electronic aspects of formation and degradation behavior on different length scales of Ni-rich NCM and Li-rich HE-NCM cathode materials in Li-ion batteries. Adv. Mater. 31, 1900985 (2019).10.1002/adma.201900985 ↗