Enhanced Toluene Combustion over Highly Homogeneous Iron Manganese Oxide Nanocatalysts
Source abstract
Abstract
Employing “redox-precipitation” reactions among MnO4+, Fe2+, and Mn2+, a facile synthetic route for highly homogeneous FeMn oxide (Fe1Mn2-RP) has been developed, which can achieve a superior catalytic performance in toluene combustion with T50 and T90 of 186 and 197 °C, respectively (500 ppm toluene/humid air, GHSV = 50,000 h–1). XRD, N2 sorption isotherms, and TEM characterization demonstrated the formation of a homogeneous Fe-Mn-O solid solution with higher surface area for the Fe1Mn2-RP catalyst. The highly homogeneous Fe-Mn-O structure can result in better low-temperature reducibility and a higher amount of oxygen electrophilic species evidenced by H2-TPR and XPS, thus significantly increasing the catalytic activity. At the same time, the Fe1Mn2-RP catalyst showed excellent water/methanol-resistance and stability, demonstrating its great potential for practical application.
Source: openalex_inverted_index · Quality: baseline
Research context
OpenAlex topics: Catalytic Processes in Materials Science · Catalysis and Oxidation Reactions · Catalysis and Hydrodesulfurization Studies
SciVX discovery tags are terminology-based. OpenAlex topics are source-provided classifications.
Affiliations
School of Environmental Science and Technology, Huazhong University of Science and Technology, Wuhan 430074, P.R. China
State Key Laboratory of High Performance Ceramic and Superfine Microstructure, Shanghai Institute of Ceramics, Chinese Academy of Sciences, Shanghai 200050, P.R. China
Funding
China Postdoctoral Science Foundation · Huazhong University of Science and Technology · State Key Laboratory of High Performance Ceramics and Superfine Microstructure
References (66)
Show source-provided references
1. 10.1016/j.jiec.2014.04.03510.1016/j.jiec.2014.04.035 ↗
2. Group, I. W. IARC Monographs on the Evaluation of the Carcinogenic Risk of Chemicals to Humans; International Agency for Research on Cancer, 2006.
3. 10.1016/j.apcatb.2014.02.00910.1016/j.apcatb.2014.02.009 ↗
4. 10.1016/j.apcatb.2010.05.02710.1016/j.apcatb.2010.05.027 ↗
5. 10.1016/j.apcatb.2011.01.02010.1016/j.apcatb.2011.01.020 ↗
6. 10.1016/j.apcatb.2012.05.01110.1016/j.apcatb.2012.05.011 ↗
7. 10.1016/S0926-3373(99)00111-310.1016/S0926-3373(99)00111-3 ↗
8. 10.1016/j.apcatb.2008.10.02210.1016/j.apcatb.2008.10.022 ↗
9. 10.1002/cctc.20100037810.1002/cctc.201000378 ↗
10. 10.1002/chem.20120041210.1002/chem.201200412 ↗
11. 10.1021/acs.est.5b0625510.1021/acs.est.5b06255 ↗
12. 10.1021/es204038j10.1021/es204038j ↗
13. 10.1021/ie070111810.1021/ie0701118 ↗
14. 10.1016/j.jcat.2013.10.01910.1016/j.jcat.2013.10.019 ↗
15. 10.1016/j.jcat.2011.12.01510.1016/j.jcat.2011.12.015 ↗
16. 10.1039/C3TA13847J10.1039/C3TA13847J ↗
17. 10.1016/j.apcatb.2009.07.01010.1016/j.apcatb.2009.07.010 ↗
18. 10.1016/j.cej.2017.07.14710.1016/j.cej.2017.07.147 ↗
19. 10.1016/j.chemosphere.2015.07.03910.1016/j.chemosphere.2015.07.039 ↗
20. 10.1016/j.jcat.2008.08.01110.1016/j.jcat.2008.08.011 ↗
21. 10.1016/j.molcata.2010.04.00910.1016/j.molcata.2010.04.009 ↗
22. 10.1021/cr300275210.1021/cr3002752 ↗
23. 10.1016/j.jssc.2004.10.03110.1016/j.jssc.2004.10.031 ↗
24. 10.1016/j.apcatb.2007.01.00810.1016/j.apcatb.2007.01.008 ↗
25. 10.1038/nature0787710.1038/nature07877 ↗
26. 10.1126/science.118826710.1126/science.1188267 ↗
27. 10.1126/science.115963910.1126/science.1159639 ↗
28. 10.1039/c3ta11566f10.1039/c3ta11566f ↗
29. 10.1016/j.catcom.2008.12.03310.1016/j.catcom.2008.12.033 ↗
30. 10.1016/j.apcatb.2010.06.00610.1016/j.apcatb.2010.06.006 ↗
31. 10.1021/cm070198n10.1021/cm070198n ↗
32. 10.1016/j.apcatb.2017.03.04910.1016/j.apcatb.2017.03.049 ↗
33. 10.1021/jp806824910.1021/jp8068249 ↗
34. 10.1016/j.apcatb.2010.11.04310.1016/j.apcatb.2010.11.043 ↗
35. 10.1016/j.jcat.2006.06.00110.1016/j.jcat.2006.06.001 ↗
36. 10.1016/j.jcat.2004.11.02010.1016/j.jcat.2004.11.020 ↗
37. 10.1021/jp100635e10.1021/jp100635e ↗
38. 10.1021/jp905482z10.1021/jp905482z ↗
39. 10.1016/S0926-3373(98)00013-710.1016/S0926-3373(98)00013-7 ↗
40. 10.1016/j.ceramint.2012.06.02210.1016/j.ceramint.2012.06.022 ↗
41. 10.1021/j100556a01110.1021/j100556a011 ↗
42. 10.1103/PhysRevB.11.217710.1103/PhysRevB.11.2177 ↗
43. 10.1016/j.apcatb.2012.01.01310.1016/j.apcatb.2012.01.013 ↗
44. 10.1016/j.apsusc.2007.09.06310.1016/j.apsusc.2007.09.063 ↗
45. 10.1016/j.apsusc.2010.10.05110.1016/j.apsusc.2010.10.051 ↗
46. 10.1016/j.apcatb.2009.10.01910.1016/j.apcatb.2009.10.019 ↗
47. 10.1039/C4NR04142A10.1039/C4NR04142A ↗
48. 10.1006/jcat.2000.306910.1006/jcat.2000.3069 ↗
49. 10.1039/c2ra00724j10.1039/c2ra00724j ↗
50. 10.1016/j.apcatb.2005.08.00410.1016/j.apcatb.2005.08.004 ↗
51. 10.1016/j.apcatb.2015.11.02010.1016/j.apcatb.2015.11.020 ↗
52. 10.1016/j.apcatb.2010.04.01810.1016/j.apcatb.2010.04.018 ↗
53. 10.1016/S0920-5861(98)00064-910.1016/S0920-5861(98)00064-9 ↗
54. 10.1016/S0920-5861(98)00026-110.1016/S0920-5861(98)00026-1 ↗
55. 10.1021/cm800832w10.1021/cm800832w ↗
56. 10.1038/nchem.124510.1038/nchem.1245 ↗
57. 10.1016/j.apcata.2012.05.01610.1016/j.apcata.2012.05.016 ↗
58. 10.1016/j.micromeso.2012.06.03010.1016/j.micromeso.2012.06.030 ↗
59. 10.1016/j.apcatb.2011.01.00110.1016/j.apcatb.2011.01.001 ↗
60. 10.1039/C5RA07072D10.1039/C5RA07072D ↗
61. 10.1016/j.apcatb.2013.04.02510.1016/j.apcatb.2013.04.025 ↗
62. 10.1002/chem.20090160110.1002/chem.200901601 ↗
63. 10.1002/anie.20045379610.1002/anie.200453796 ↗
64. 10.1016/j.apcatb.2011.02.01910.1016/j.apcatb.2011.02.019 ↗
65. 10.1016/j.apcatb.2013.04.05110.1016/j.apcatb.2013.04.051 ↗
66. 10.1021/es903199710.1021/es9031997 ↗