The influence of an AlN seeding layer on nucleation of self-assembled GaN nanowires on silicon substrates

Abstract Gallium nitride (GaN)-based nanowires (NWs) have attracted much attention for the fabrication of novel nanostructured devices. In this paper, the influence of an AlN seeding layer on the nucleation of self-assembled GaN NWs grown by plasma-assisted molecular beam epitaxy (MBE) on Si (111) substrates has been investigated. Not only is the formation of a two-dimensional compact GaN layer at the bottom of the NWs suppressed, but also a high density of vertically aligned well-separated GaN NWs originating from GaN islands are successfully obtained after introducing annealing and nitridation processes. Scanning electronic microscope and transmission electron microscope measurements show that the NWs have a high crystalline wurtzite structure nearly free of dislocations and stacking faults and the NW diameter remains constant over almost the entire length. Due to the temperature-dependent diffusion length of Ga adatoms during the nucleation process, the formation of well-separated NWs relies on the distribution and morphology of the underlying AlN seeding layer. Moreover, the SiN _x layer served as mask to inhibit coalescence at the nucleation sites. The developed growth processes and the obtained results provide a viable path facilitating the use of MBE growth techniques to fabricate III-nitride NW-based materials and related devices on Si substrates.