Fabrication and Characterization of Diatomite Functionalized Cellulose Acetate Nanofibers
Source abstract
Abstract
Cellulose acetate (CA) nanofiber membranes incorporated with diatomite (DE) were prepared by electrospinning to produce electrospun nanofiber membranes with high specific surface area and high porosity with fine pores. When the DE percentage increased from 0 to 30%, the water contact angle (WCA) of the membranes increased from 86.21° to 118.44°, indicating that neat CA nanofibers were more hydrophilic than CA/DE nanofibers and had a better wetting tendency. CA, CA-10DE, and CA-20DE nanofiber membranes showed a mean flow pore size (MFP) of 2.941, 2.681, and 2.408 μm, respectively, with narrow pore size distributions. However, the CA-30DE nanofiber membrane showed a smaller MFP size of 0.5014 μm. CA nanofibers were produced in the range of 206.31 to 281.13 nm. The dye removal ability of these membranes was tested using an aqueous solution of C.I. Reactive Red 141.
Source: crossref · Quality: baseline
Research context
OpenAlex topics: Electrospun Nanofibers in Biomedical Applications · Advanced Cellulose Research Studies · Microplastics and Plastic Pollution
SciVX discovery tags are terminology-based. OpenAlex topics are source-provided classifications.
Affiliations
Pamukkale University
References (43)
Show source-provided references
1. 10.1016/j.clay.2008.07.00910.1016/j.clay.2008.07.009 ↗
2. 10.1016/j.apsusc.2015.01.14910.1016/j.apsusc.2015.01.149 ↗
3. 10.1016/j.desal.2007.03.00310.1016/j.desal.2007.03.003 ↗
4. 10.1016/S0043-1354(01)00071-910.1016/S0043-1354(01)00071-9 ↗
5. 10.1016/j.jenvman.2003.09.00510.1016/j.jenvman.2003.09.005 ↗
6. 10.1016/j.cej.2003.11.02910.1016/j.cej.2003.11.029 ↗
7. 10.1016/j.clay.2013.08.00810.1016/j.clay.2013.08.008 ↗
8. 10.1016/j.jcis.2004.08.16610.1016/j.jcis.2004.08.166 ↗
9. 10.1016/j.jhazmat.2011.09.01610.1016/j.jhazmat.2011.09.016 ↗
10. 10.1016/j.carbpol.2010.08.05410.1016/j.carbpol.2010.08.054 ↗
11. 10.1016/j.polymer.2010.10.01510.1016/j.polymer.2010.10.015 ↗
12. 10.1016/j.carbon.2012.02.05610.1016/j.carbon.2012.02.056 ↗
13. 10.1016/j.colsurfa.2009.05.02910.1016/j.colsurfa.2009.05.029 ↗
14. 10.1007/s10965-009-9368-610.1007/s10965-009-9368-6 ↗
15. 10.1142/9789812567611_000210.1142/9789812567611_0002 ↗
16. Akduman C. · IOP Conf. Ser-Mat. Sci. · 2017 · 254 · 102001
17. 10.1016/S0266-3538(03)00178-710.1016/S0266-3538(03)00178-7 ↗
18. 10.1080/0098644100362599710.1080/00986441003625997 ↗
19. 10.1016/j.biomaterials.2008.01.01110.1016/j.biomaterials.2008.01.011 ↗
20. Teo W.E. · J. Healthc. Nutr. Technol. · 2006 · 1 · 918
21. Interlab. http://www.interlab.com.tr/assets/upload/editor/isolab_2015_catalog_61.pdf. (accessed July 2018).
22. Sigma Aldrich. https://www.sigmaaldrich.com/catalog/product/aldrich/180955?lang=en®ion=TR. (accessed July 2018).
23. 10.1002/app.2323710.1002/app.23237 ↗
24. 10.1007/s10311-005-0109-810.1007/s10311-005-0109-8 ↗
25. 10.1016/j.memsci.2016.07.01910.1016/j.memsci.2016.07.019 ↗
26. 10.1016/j.jcis.2005.10.05810.1016/j.jcis.2005.10.058 ↗
27. 10.1007/s10853-017-1370-510.1007/s10853-017-1370-5 ↗
28. 10.1016/j.cej.2011.10.01110.1016/j.cej.2011.10.011 ↗
29. Peacor D. B. · Zeitschrift für Kristallographie-Cryst Mater. · 1973 · 138 · 274
30. 10.1007/s00269-005-0005-610.1007/s00269-005-0005-6 ↗
31. 10.1107/S056774087900412X10.1107/S056774087900412X ↗
32. 10.1007/s00269005024610.1007/s002690050246 ↗
33. 10.1016/j.jmst.2016.02.01210.1016/j.jmst.2016.02.012 ↗
34. 10.1007/s10853-014-8270-810.1007/s10853-014-8270-8 ↗
35. 10.1016/j.memsci.2005.04.04410.1016/j.memsci.2005.04.044 ↗
36. 10.1016/j.polymer.2004.01.02610.1016/j.polymer.2004.01.026 ↗
37. 10.1016/j.apsusc.2014.03.13810.1016/j.apsusc.2014.03.138 ↗
38. 10.3390/membranes702002710.3390/membranes7020027 ↗
39. 10.1016/j.carbpol.2011.10.04610.1016/j.carbpol.2011.10.046 ↗
40. 10.1007/978-3-642-38649-7_2610.1007/978-3-642-38649-7_26 ↗
41. 10.1016/j.desal.2015.09.00910.1016/j.desal.2015.09.009 ↗
42. Adsorption. Encycloaedia Britannica. https://www.britannica.com/science/adsorption. (accessed July 2018).
43. Advantecmfs Inc. http://www.advantecmfs.com/catalog/filt/membrane.pdf. (accessed July 2018).