Catalytic oxidation of CH 4 over nonprecious Ni/CeO 2 catalysts has attracted wide attention. Controlling the morphology of a CeO 2 support can enhance the CH 4 oxidation activity without changing the catalyst composition. Herein, a series of 2 wt % Ni/CeO 2 nanocatalysts with different CeO 2 support morphologies (nanoparticles (P), rods (R), cubes (C)) and synthetic procedures (precipitation, sol-gel (SG)) were evaluated for their CH 4 oxidation performance. The redox properties of CeO 2 supports and corresponding Ni loaded catalysts were characterized by H 2 -temperature-programmed reduction and oxygen storage capacity (OSC) measurements. The relationship among the CeO 2 morphologies, surface areas, redox properties, and CH 4 oxidation activity for both CeO 2 supports and Ni/CeO 2 catalysts was established. The findings suggest that CeO 2 -R has a greater amount of surface oxygen vacancies as well as an improved OSC and CH 4 oxidation activity compared to CeO 2 -P and CeO 2 -C supports. The same CH 4 oxidation activity pattern was observed for the Ni containing catalysts (Ni/CeO 2 -R > Ni/CeO 2 -P > Ni/CeO 2 -C). Increasing the CeO 2 surface area by using a sol-gel synthesis method (CeO 2 -SG) improved the amount of surface oxygen vacancies and CH 4 oxidation performance of CeO 2 -SG and Ni/CeO 2 -SG compared to CeO 2 -R and Ni/CeO 2 -R, respectively. Finally, all studied Ni/CeO 2 nanocatalysts showed improved hydrothermal stability compared to conventional Pd/Al 2 O 3 .
Source: openalex_inverted_index · Quality: baseline
Affiliations
Department of Chemical and Biological Engineering, University at Buffalo, The State University of New York, Buffalo, New York 14260, United States
Department of Chemical and Biological Engineering and Center for Micro-Engineered Materials, University of New Mexico, Albuquerque, New Mexico 87131, United States
Energy and Transportation Sciences Division, Oak Ridge National Laboratory, Oak Ridge, Tennessee 37831, United States
Manufacturing Science Division, Oak Ridge National Laboratory, Oak Ridge, Tennessee 37831, United States
Funding
Oak Ridge National Laboratory · Basic Energy Sciences · Graduate Student Association, University at Buffalo · Vehicle Technologies Program · U.S. Department of Energy · NSF MRI · Department of Chemical and Biological Engineering, University at Buffalo