Particle size, grain size and γ-MgH2effects on the desorption properties of nanocrystalline commercial magnesium hydride processed by controlled mechanical milling

R A Varin, T Czujko, Z Wronski

Nanotechnology· Volume 17· Issue 15
Publisher page

Abstract

The hydrogen desorption properties of commercial nanocrystalline magnesium hydride (Tego Magnan® from Degussa–Goldschmidt) processed by controlled mechanical milling (CMM) are investigated. A profound effect of the powder particle size on the hydrogen desorption characteristics has been observed. The onset (TON) and peak hydrogen desorption temperatures measured by differential scanning calorimetry (DSC) decrease initially slowly with decreasing mean particle size of hydride, and when the particle size reaches a certain critical threshold value, the desorption temperatures start decreasing more rapidly with further decrease of particle size. The total drop of desorption temperature from its initial value for the as-received MgH2 to the value attained for the milled MgH2 having a particle size of ∼500–600 nm is within the range 40–60 °C. The metastable γ-MgH2 hydride coexists with the stable nanocrystalline β-MgH2 in the microstructure of the MgH2 powders ball milled for 10 h and longer. Quantitative evidence shows that two factors, namely the refined powder particle size and the γ-MgH2 phase residing within the powder particles, acting additively, are responsible for a substantial reduction of the hydrogen desorption temperature of MgH2 hydride.
Source: openalex_inverted_index · Quality: baseline

Research context

OpenAlex topics: Hydrogen Storage and Materials · Ammonia Synthesis and Nitrogen Reduction · Superconductivity in MgB2 and Alloys

SciVX discovery tags are terminology-based. OpenAlex topics are source-provided classifications.

References (31)

Show source-provided references
1. 10.1002/adem.20050002210.1002/adem.200500022 ↗
2. 10.1002/adma.20030655710.1002/adma.200306557 ↗
3. 10.1007/s00339010078310.1007/s003390100783 ↗
4. 10.1007/s00339010077210.1007/s003390100772 ↗
5. 10.1016/S0925-8388(99)00073-010.1016/S0925-8388(99)00073-0 ↗
6. 10.1038/3510463410.1038/35104634 ↗
7. Ritter J A · Mater. Today · 2003 · 1810.1016/S1369-7021(03)00921-0 ↗
8. Cho A · Science · 2004 · 305 · 965
9. Varin R A · J. Alloys Compounds · 2006
10. Czujko T Varin R A Chiu Ch Wronski Z Petrovic J J Anderson I E Adams T M Sandrock G Legzdins C F Stevenson J W Yang Z G · MS&T’05: Proc. Int. Symp. on the Materials for the Hydrogen Economy: Materials Science and Technology Conference and Exhibition 2005 · 2005 · 3
11. 10.1016/0921-5093(91)90989-Z10.1016/0921-5093(91)90989-Z ↗
12. Klug H P · X-ray Diffraction Procedures for Polycrystalline and Amorphous Materials · 1974 · 618
13. 10.1016/j.jallcom.2003.12.04010.1016/j.jallcom.2003.12.040 ↗
14. 10.1016/j.apsusc.2005.04.01810.1016/j.apsusc.2005.04.018 ↗
15. 10.1016/0025-5408(80)90197-X10.1016/0025-5408(80)90197-X ↗
16. 10.1016/S0925-8388(99)00474-010.1016/S0925-8388(99)00474-0 ↗
17. Varin R A · Nanotechnology · 2005 · 16 · 226110.1088/0957-4484/16/10/048 ↗
18. 10.1016/j.jallcom.2004.08.04810.1016/j.jallcom.2004.08.048 ↗
19. 10.1016/j.jallcom.2004.05.01810.1016/j.jallcom.2004.05.018 ↗
20. 10.1016/j.actamat.2003.08.03210.1016/j.actamat.2003.08.032 ↗
21. Kojima Y · J. Alloys Compounds · 2006
22. 10.1016/S0925-8388(00)00710-610.1016/S0925-8388(00)00710-6 ↗
23. 10.1016/j.jallcom.2004.12.17610.1016/j.jallcom.2004.12.176 ↗
24. 10.1021/ja051508a10.1021/ja051508a ↗
25. 10.1016/S0925-8388(00)01460-210.1016/S0925-8388(00)01460-2 ↗
26. 10.1016/0360-3199(86)90082-010.1016/0360-3199(86)90082-0 ↗
27. 10.1016/j.jallcom.2005.05.03710.1016/j.jallcom.2005.05.037 ↗
28. 10.1016/j.jallcom.2004.07.00110.1016/j.jallcom.2004.07.001 ↗
29. 10.1016/j.jallcom.2005.02.04310.1016/j.jallcom.2005.02.043 ↗
30. 10.1016/j.jallcom.2004.08.10210.1016/j.jallcom.2004.08.102 ↗
31. 10.1016/j.jcat.2006.01.03110.1016/j.jcat.2006.01.031 ↗