Internal charge behaviour of nanocomposites
Source abstract
Abstract
The incorporation of 23 nm titanium dioxide nanoparticles into an epoxy matrix to form a nanocomposite structure is described. It is shown that the use of nanometric particles results in a substantial change in the behaviour of the composite, which can be traced to the mitigation of internal charge when a comparison is made with conventional TiO2 fillers. A variety of diagnostic techniques (including dielectric spectroscopy, electroluminescence, thermally stimulated current and photoluminescence) have been used to augment pulsed electro-acoustic space charge measurement to provide a basis for understanding the underlying physics of the phenomenon. It would appear that, when the size of the inclusions becomes small enough, they act cooperatively with the host structure and cease to exhibit interfacial properties, leading to Maxwell–Wagner polarization. It is postulated that the particles are surrounded by high charge concentrations in the Gouy–Chapman–Stern layer. Since nanoparticles have very high specific areas, these regions allow limited charge percolation through nano-filled dielectrics. The practical consequences of this have also been explored in terms of the electric strength exhibited. It would appear that there was a window in which real advantages accrue from the nano-formulated material. An optimum loading of about 10 % (by weight) is indicated. (Some figures in this article are in colour only in the electronic version) 1. Introduction and
Source: openalex_inverted_index · Quality: baseline
Research context
OpenAlex topics: High voltage insulation and dielectric phenomena · Dielectric materials and actuators · Smart Materials for Construction
SciVX discovery tags are terminology-based. OpenAlex topics are source-provided classifications.
References (24)
Show source-provided references
1. 10.1109/94.32665310.1109/94.326653 ↗
2. Frechette M F · Annual Report of the Conf. on Electrical Insulation and Dielectric Phenomena · 2001 · pp 92
3. Sabuni H · J. Mater. Sci. · 1976 · 11 · 157410.1007/BF00540892 ↗
4. Nelson J K · Engineering Dielectrics · 1993 · 2A
5. Crine J-P · Appl. Phys. Commun. · 1985 · 5 · 139
6. Dissado L A · Electrical Degradation and Breakdown in Polymers · 199210.1049/PBED009E ↗
7. Nelson J K Fothergill J C Dissado L A Peasgood W · Annual Report of the Conf. on Electrical Insulation and Dielectric Phenomena · 2002 · pp 295
8. Jonscher A K · Dielectric Relaxation In Solids · 1983
9. Dissado L A · J. Chem. Soc. Faraday Trans. · 1984 · 80 · 29110.1039/f29848000291 ↗
10. Chapman D L · Phil. Mag. · 1913 · 25 · 47510.1080/14786440408634187 ↗
11. 10.1016/S0167-2738(01)00677-410.1016/S0167-2738(01)00677-4 ↗
12. Lewis T J · 2003
13. Alison J · Meas. Sci. Technol. · 1998 · 9 · 173710.1088/0957-0233/9/10/014 ↗
14. Bambery K R Fleming R J · Annual Report on IEEE Conf. on Electrical Insulation and Dielectric Phenomena pub no. 03CH37471 · 2003 · 2810.1109/CEIDP.2003.1254786 ↗
15. Griseri V · 2000
16. Mason J H · Proc. IEE · 1955 · 102C · 254
17. 10.1109/94.98389910.1109/94.983899 ↗
18. Kawamoto A · Proc. 3rd Int. Conf. on Properties and Applications of Dielectric Materials · 1991 · pp 61910.1109/ICPADM.1991.172136 ↗
19. 10.1103/PhysRevLett.66.302010.1103/PhysRevLett.66.3020 ↗
20. Henk P O · High Perform. Polym. · 1999 · 11 · 28110.1088/0954-0083/11/3/304 ↗
21. Henk P O Henriksen M Holbell J T Iqbal J · Proc. Nordic Insulation Symp. · 1992 · pp 4.2:1
22. Artbauer J · J. Phys. D: Appl. Phys. · 1996 · 29 · 44610.1088/0022-3727/29/2/024 ↗
23. van Turnhout J · Electrets · 1980
24. 10.1021/ma020482u10.1021/ma020482u ↗