Monolayer MoS 2 growth at the Au–SiO 2 interface
Source abstract
Abstract
Monolayer MoS 2 was grown directly at the interface between Au and SiO 2 by CVD.
Only a short abstract or summary was supplied by the source.
Source: crossref · Quality: short
Research context
OpenAlex topics: 2D Materials and Applications · MXene and MAX Phase Materials · Ferroelectric and Negative Capacitance Devices
SciVX discovery tags are terminology-based. OpenAlex topics are source-provided classifications.
Affiliations
Department of Physics
Tokyo Metropolitan University
Hachioji
Japan
Nanoelectronics Research Institute (NeRI)
National Institute of Advanced Industrial Science and Technology (AIST)
Tsukuba
Nanomaterials Research Institute (NMRI)
Funding
Core Research for Evolutional Science and Technology · Japan Society for the Promotion of Science
References (36)
Show source-provided references
1. Wang · Nat. Nanotechnol. · 2012 · 7 · 69910.1038/nnano.2012.193 ↗
2. Xia · Nat. Photonics · 2014 · 8 · 89910.1038/nphoton.2014.271 ↗
3. Mak · Nat. Photonics · 2016 · 10 · 21610.1038/nphoton.2015.282 ↗
4. Radisavljevic · Nat. Nanotechnol. · 2011 · 6 · 14710.1038/nnano.2010.279 ↗
5. Mak · Nat. Nanotechnol. · 2012 · 7 · 49410.1038/nnano.2012.96 ↗
6. Mak · Science · 2014 · 344 · 148910.1126/science.1250140 ↗
7. Zheng · Adv. Opt. Mater. · 2018 · 6 · 180042010.1002/adom.201800420 ↗
8. Lee · Adv. Mater. · 2012 · 24 · 232010.1002/adma.201104798 ↗
9. Zhan · Small · 2012 · 8 · 96610.1002/smll.201102654 ↗
10. Yu · Sci. Rep. · 2013 · 3 · 186610.1038/srep01866 ↗
11. Li · Appl. Mater. Today · 2015 · 1 · 6010.1016/j.apmt.2015.09.001 ↗
12. Zhou · Nature · 2018 · 556 · 35510.1038/s41586-018-0008-3 ↗
13. Song · Angew. Chem., Int. Ed. · 2014 · 53 · 126610.1002/anie.201309474 ↗
14. Gao · Nat. Commun. · 2015 · 6 · 856910.1038/ncomms9569 ↗
15. Shi · Nano Lett. · 2012 · 12 · 278410.1021/nl204562j ↗
16. Kobayashi · ACS Nano · 2015 · 9 · 405610.1021/acsnano.5b00103 ↗
17. Wang · ACS Nano · 2015 · 9 · 524610.1021/acsnano.5b00655 ↗
18. Zhao · 2D Mater. · 2016 · 3 · 02502710.1088/2053-1583/3/2/025027 ↗
19. Okada · Sci. Rep. · 2017 · 7 · 32210.1038/s41598-017-00068-0 ↗
20. Uchida · ACS Nano · 2018 · 12 · 623610.1021/acsnano.8b03055 ↗
21. Gao · ACS Nano · 2016 · 10 · 262810.1021/acsnano.5b07677 ↗
22. Liu · Nature · 2018 · 557 · 69610.1038/s41586-018-0129-8 ↗
23. Wang · Nature · 2019 · 568 · 7010.1038/s41586-019-1052-3 ↗
24. Kojima · Nanoscale · 2019 · 11 · 1279810.1039/C9NR01481K ↗
25. Li · ACS Nano · 2018 · 12 · 897010.1021/acsnano.8b02409 ↗
26. Lee · ACS Nano · 2010 · 4 · 269510.1021/nn1003937 ↗
27. Li · Adv. Funct. Mater. · 2012 · 22 · 138510.1002/adfm.201102111 ↗
28. Splendiani · Nano Lett. · 2010 · 10 · 127110.1021/nl903868w ↗
29. Li · Nat. Mater. · 2018 · 17 · 53510.1038/s41563-018-0055-z ↗
30. Wu · ACS Nano · 2013 · 7 · 276810.1021/nn4002038 ↗
31. Song · Chem. – Eur. J. · 2019 · 25 · 233710.1002/chem.201805452 ↗
32. Sangiorgi · J. Am. Ceram. Soc. · 1988 · 71 · 74210.1111/j.1151-2916.1988.tb06407.x ↗
33. Todeschini · ACS Appl. Mater. Interfaces · 2017 · 9 · 3737410.1021/acsami.7b10136 ↗
34. Kang · Nature · 2015 · 520 · 65610.1038/nature14417 ↗
35. Kobayashi · ACS Nano · 2019 · 13 · 752710.1021/acsnano.8b07991 ↗
36. Ahn · Adv. Mater. · 2015 · 27 · 522310.1002/adma.201501678 ↗