Size selection and thin-film assembly of MoS 2 elucidates thousandfold conductivity enhancement in few-layer nanosheet networks
Source abstract
Abstract
Printed electronics based on liquid-exfoliated nanosheet networks are limited by inter-nanosheet junctions and thick films which hinder field-effect gating. Here, few-layer molybdenum disulfide nanosheets are assembled by Langmuir deposition into thin films, and size selection is shown to lead to a thousandfold conductivity enhancement with potential applicability to all nanosheet networks.
Source: openalex_inverted_index · Quality: candidate unverified · Source record ↗
Research context
OpenAlex topics: 2D Materials and Applications · Graphene research and applications · Perovskite Materials and Applications
SciVX discovery tags are terminology-based. OpenAlex topics are source-provided classifications.
Affiliations
University of Sussex, Brighton, BN1 9RH, UK
University of Brighton, Brighton, BN2 4GJ, UK
References (39)
Show source-provided references
1. Carey · Nat. Commun. · 2017 · 8 · 120210.1038/s41467-017-01210-2 ↗
2. Kelly · Science · 2017 · 356 · 6910.1126/science.aal4062 ↗
3. Worsley · ACS Nano · 2019 · 13 · 5410.1021/acsnano.8b06464 ↗
4. Finn · J. Mater. Chem. C · 2014 · 2 · 92510.1039/C3TC31993H ↗
5. Higgins · Adv. Funct. Mater. · 2018 · 1804387
6. Ippolito · Nat. Nanotechnol. · 2021 · 1
7. Lin · Nature · 2018 · 562 · 25410.1038/s41586-018-0574-4 ↗
8. Carey · Adv. Electron. Mater. · 2021 · 7 · 210011210.1002/aelm.202100112 ↗
9. Neilson · ACS Appl. Mater. Interfaces · 2020 · 12 · 2512510.1021/acsami.0c03794 ↗
10. Cote · J. Am. Chem. Soc. · 2009 · 131 · 104310.1021/ja806262m ↗
11. Gengler · Small · 2010 · 6 · 3510.1002/smll.200901120 ↗
12. Zheng · ACS Nano · 2011 · 5 · 603910.1021/nn2018683 ↗
13. Kim · Nanoscale · 2013 · 5 · 1236510.1039/c3nr02907g ↗
14. Fahimi · Carbon · 2013 · 64 · 43510.1016/j.carbon.2013.07.096 ↗
15. Zhang · J. Mater. Chem. C · 2017 · 5 · 1127510.1039/C7TC02637D ↗
16. Kalosi · Langmuir · 2019 · 35 · 980210.1021/acs.langmuir.9b01000 ↗
17. Large · Langmuir · 2017 · 33 · 1476610.1021/acs.langmuir.7b03867 ↗
18. Liu · Appl. Phys. Lett. · 2014 · 105 · 20190510.1063/1.4901836 ↗
19. Backes · ACS Nano · 2016 · 10 · 158910.1021/acsnano.5b07228 ↗
20. Ogilvie · 2D Mater. · 2019 · 6 · 03100210.1088/2053-1583/ab0dc3 ↗
21. Backes · Nat. Commun. · 2014 · 5 · 457610.1038/ncomms5576 ↗
22. Backes · Nanoscale · 2016 · 8 · 431110.1039/C5NR08047A ↗
23. Mao · Small · 2013 · 9 · 131210.1002/smll.201202982 ↗
24. Cunningham · J. Mater. Chem. C · 2013 · 1 · 689910.1039/c3tc31402b ↗
25. Cunningham · Nanoscale · 2014 · 7 · 19810.1039/C4NR04951A ↗
26. Lee · Adv. Mater. · 2011 · 23 · 417810.1002/adma.201101013 ↗
27. Choi · Adv. Mater. · 2012 · 24 · 583210.1002/adma.201201909 ↗
28. Radisavljevic · Nat. Nanotechnol. · 2011 · 6 · 14710.1038/nnano.2010.279 ↗
29. Das · Nano Lett. · 2013 · 13 · 10010.1021/nl303583v ↗
30. McDonnell · ACS Nano · 2014 · 8 · 288010.1021/nn500044q ↗
31. Cunningham · Nanoscale · 2012 · 4 · 626010.1039/c2nr31782f ↗
32. Kelly · 2D Mater. · 2017 · 4 · 04100610.1088/2053-1583/aa8442 ↗
33. Zhou · Nano Lett. · 2013 · 13 · 261510.1021/nl4007479 ↗
34. Komsa · Phys. Rev. Lett. · 2012 · 109 · 03550310.1103/PhysRevLett.109.035503 ↗
35. Liu · Appl. Phys. Lett. · 2013 · 103 · 18311310.1063/1.4824893 ↗
36. Amorim Graf · Nanoscale · 2019 · 11 · 1555010.1039/C9NR04974F ↗
37. Varrla · Chem. Mater. · 2015 · 27 · 112910.1021/cm5044864 ↗
38. Boland · Nanoscale Adv. · 2019 · 1 · 156010.1039/C8NA00241J ↗
39. Large · Adv. Mater. Technol. · 2020 · 5 · 200028410.1002/admt.202000284 ↗