A platinum–nickel bimetallic nanocluster ensemble-on-polyaniline nanofilm for enhanced electrocatalytic oxidation of dopamine

We report a new approach to design flexible functional material platforms based on electropolymerized polyaniline (PANI) polymer nanofilms modified with bimetallic nanoclusters (NCs) for efficient electro-oxidation of small organic molecules. Composition defined ligand free Pt_0.75Ni_0.25 NCs were synthesized in the gas phase using the Cluster Beam Deposition (CBD) technology and characterized using RToF, HAADF-STEM, XAFS and XPS. NCs were then directly deposited on PANI coated templates to construct electrodes. Dopamine (DP) molecules were used as a representative organic analyte and the influence of the NC-PANI hybrid atomistic structure on the electrochemical and electrocatalytic performance was investigated. The as prepared, nearly monodispersed, Pt_0.75Ni_0.25 NCs of ca. 2 nm diameter featuring a PtOx surface combined with a shallow platelet-like Ni-O(OH) phase formed a densely packed active surface on PANI at ultralow metal coverages. Electrochemical measurements (EIS and CV) show a 2.5 times decrease in charge transfer resistance and a remarkable 6-fold increase at lower potential in the mass activity for Pt_0.75Ni_0.25 NCs in comparison with their pure Pt counterparts. The enhanced electrochemical performance of the Pt_0.75Ni_0.25 NC hybrid's interface is ascribed to the formation of mixed Pt metal and Ni-O(OH) phases at the surface of the alloyed PtNi cores of the bimetallic NCs under electrochemical conditions combined with an efficient charge conduction pathway between NCs.