Rapid preparation of ultra-fine and well-dispersed SnO ₂ nanoparticles via a double hydrolysis reaction for lithium storage

An efficient and rapid method is reported for preparing ultra-fine and well-dispersed SnO₂ nanoparticles in a large scale. A simple double hydrolysis reaction between SnO₃^2- and Fe³⁺ ions was masterly used to form a stable colloid system, in which colloidal particles of H₂SnO₃ with negative charges and Fe(OH)₃ with positive charges electrostatically interact with each other and form honeycomb-like "core-shell" units. Through the hydrothermal reaction, the units are easily transformed into SnO₂@FeO(OH) structures. Ultra-fine and well-dispersed SnO₂ particles with less than 6 nm diameter were finally obtained with a high yield by further etching using hydrochloric acid. When used as anode materials for lithium ion batteries, the ultra-fine SnO₂ particles can be easily dispersed into the carbon networks originating from the carbon source of glucose during the hydrothermal reaction. Electrochemical tests confirmed that these ultra-fine SnO₂/C materials were endowed with excellent cyclic stability and C-rate performance. Even at a 1.56 A g^-1 (2C) high current density, the reversible capacity could be maintained at 710 mA h g^-1 after 100 cycles owing to the ultra-fine particle size of SnO₂ and the rich carbon networks.