Construction board resistance to accelerated aging

Physical and mechanical properties were evaluated for industrial and laboratory boards intended to be used in the construction industry. The boards were subjected to accelerated aging tests including resistance to humidity in the conditions of cyclic test in accordance with EN 321 (2002), and determination of dimensional changes resulting from changes in relative humidity according to EN 318 (2002). The greatest changes were observed after one test cycle. Moreover, the boards made of fine chips demonstrated slightly higher resistance to the tested factors. Although laboratory boards showed a much lower density, their behavior following the exposure to the assessed factors was similar to that of industrial plates.