Nanoindentation in Tin/Nbn Multilayers and Thin Films Examined Using Transmission Electron Microscopy

Abstract Nanoindentation allows the hardness of thin coatings and synthetic multilayer structures to be measured, since indentation depths can be as little as a few 10s of nm. In combination with the cross-sectional transmission electron microscopy (TEM) analysis described here it is possible to observe the deformation structure under an indent, and potentially to understand deformation mechanisms on a nm scale in a wide variety of materials. Synthetic multilayers are a particularly interesting system to investigate. Variations in hardness with the multilayer compositional repeat distance (A) have been reported for several systems. The highest hardnesses, which are in excess of what a simple “rule of mixtures” would predict, occur in nitride multilayers at A ∼5nm. Here we present some preliminary results showing the deformation structure in both a monolithic NbN film and a TiN/NbN multilayer in which both components have the rQck salt structure with lattice parameters 0.424nm (TiN) and 0.439nm (NbN).