Minimizing Transmission Electron Microscopy Beam Damage during the Study of Surface Reactions on Sodium Chloride

Electron beam damage is a significant limitation for transmission electron microscopy (TEM) studies of beam-sensitive samples. An approach for studying surface reactions on alkali halide crystals using 200 kV TEM is presented. Experiments were designed to monitor the reaction of NaCl crystals with HNO₃ gas followed by water vapor to form solid NaNO₃. During beam damage experiments, TEM micrographs record structural changes to both NaCl and NaNO₃, including dislocation loops, void formation, and decomposition. Sample decomposition can be successfully minimized by a combination of commonly used techniques: (1) focusing the beam adjacent to the area of interest, (2) lowering the electron density, (3) choosing to image larger (micrometer- versus submicrometer-sized) alkali halide crystals, and (4) lowering temperature by the use of a liquid nitrogen cooling stage. From these results, additional studies were designed that monitored sequential experiments. Sensitive micrometer-sized sodium chloride single crystals before and after exposure to nitric acid vapor and water vapor and the subsequent growth of submicrometer-sized sodium nitrate single crystals could then be successfully imaged using TEM.