journal article·2022-06Open access

The Phase Transformations Induced by High-Pressure Torsion in Ti–Nb-Based Alloys

Anna Korneva, Boris Straumal, Askar Kilmametov, Lidia Lityńska-Dobrzyńska, Robert Chulist, Łukasz Gondek, Paweł Zięba

Microscopy and Microanalysis· Volume 28· Issue 3

Abstract

The study of the fundamentals of the α → ω and β → ω phase transformations induced by high-pressure torsion (HPT) in Ti–Nb-based alloys is presented in the current work. Prior to HPT, three alloys with 5, 10, and 20 wt% of Nb were annealed in the temperature range of 700–540°C in order to obtain the (α + β)-phase state with a different amount of the β-phase. The samples were annealed for a long time in order to reach equilibrium Nb content in the α-solid solution. Scanning electron microscope (SEM), transmission electron microscopy, and X-ray diffraction techniques were used for the characterization of the microstructure evolution and phase transformations. HPT results in a strong grain refinement of the microstructure, a partial transformation of the α-phase into the ω-phase, and a complete β → ω phase transformation. Two kinds of the ω-phase with different chemical compositions were observed after HPT. The first one was formed from the β-phase, enriched in Nb, and the second one from the almost Nb-pure α-phase. It was found that the α → ω phase transformation depends on the Nb content in the initial α-Ti phase. The less the amount of Nb in the α-phase, the more the amount of the α-phase is transformed into the ω-phase.
Source: crossref · Quality: baseline

Research context

OpenAlex topics: Titanium Alloys Microstructure and Properties · Intermetallics and Advanced Alloy Properties · Advanced materials and composites

SciVX discovery tags are terminology-based. OpenAlex topics are source-provided classifications.

References (18)

Show source-provided references
1. 10.1007/BF0287370410.1007/BF02873704 ↗
2. Evolution of microstructure and microhardness in HPT titanium during annealing
3. 10.1007/s11837-006-0213-710.1007/s11837-006-0213-7 ↗
4. 10.1016/j.jallcom.2014.12.15910.1016/j.jallcom.2014.12.159 ↗
5. 10.1016/j.msea.2014.07.03010.1016/j.msea.2014.07.030 ↗
6. 10.1002/adem.20180015810.1002/adem.201800158 ↗
7. 10.1088/1468-6996/14/5/05500410.1088/1468-6996/14/5/055004 ↗
8. 10.3139/146.10160610.3139/146.101606 ↗
9. 10.1016/j.acme.2013.07.00210.1016/j.acme.2013.07.002 ↗
10. 10.1107/S002188981003049910.1107/S0021889810030499 ↗
11. 10.1016/j.matchar.2021.11093710.1016/j.matchar.2021.110937 ↗
12. 10.3103/S106287381809020410.3103/S1062873818090204 ↗
13. 10.1016/j.scriptamat.2017.04.01010.1016/j.scriptamat.2017.04.010 ↗
14. 10.1016/j.actamat.2017.10.05110.1016/j.actamat.2017.10.051 ↗
15. 10.1103/PhysRevLett.91.02570110.1103/PhysRevLett.91.025701 ↗
16. 10.2320/matertrans.46.107010.2320/matertrans.46.1070 ↗
17. 10.1016/j.scriptamat.2013.08.02810.1016/j.scriptamat.2013.08.028 ↗
18. 10.1016/j.pmatsci.2008.06.00410.1016/j.pmatsci.2008.06.004 ↗