In situ TEM Characterization of Microstructure Evolution and Mechanical Behavior of the 3D-Printed Inconel 718 Exposed to High Temperature
Source abstract
Abstract
This in situ transmission electron microscopy work presents a nanoscale characterization of the microstructural evolution in 3D-printed Inconel 718 (IN718) while exposed to elevated temperature and an associated change in the mechanical property under tensile loading. Here, we utilized a specially designed specimen shape that enables tensile testing of nano-sized thin films without off-plane deformations. Additionally, it allows a seamless transition from the in situ heating to tensile experiment using the same specimen, which enables a direct correlation of the microstructure and the mechanical property of the sample. The method was successfully used to observe the residual stress relaxation and the formation of incoherent γ′ precipitates when temperature was increased to 700°C. The subsequent in situ tensile test revealed that the exposure of the as-printed IN718 to a high temperature without full heat treatment (solutionizing and double aging) leads to loss of ductility.
Source: openalex_inverted_index · Quality: candidate unverified · Source record ↗
Research context
OpenAlex topics: Additive Manufacturing Materials and Processes · Additive Manufacturing and 3D Printing Technologies · High Entropy Alloys Studies
SciVX discovery tags are terminology-based. OpenAlex topics are source-provided classifications.
References (68)
Show source-provided references
1. 10.1016/j.mattod.2017.11.00410.1016/j.mattod.2017.11.004 ↗
2. 10.1063/1.184459410.1063/1.1844594 ↗
3. 10.1016/j.msea.2016.03.08810.1016/j.msea.2016.03.088 ↗
4. 10.1016/j.matdes.2009.11.03210.1016/j.matdes.2009.11.032 ↗
5. 10.1016/j.actbio.2019.05.05610.1016/j.actbio.2019.05.056 ↗
6. 10.1103/PhysRevB.73.24541010.1103/PhysRevB.73.245410 ↗
7. 10.1016/j.matdes.2013.08.08510.1016/j.matdes.2013.08.085 ↗
8. 10.1021/nn303762310.1021/nn3037623 ↗
9. 10.1038/s41467-019-12047-210.1038/s41467-019-12047-2 ↗
10. 10.1016/j.matdes.2016.12.02610.1016/j.matdes.2016.12.026 ↗
11. 10.1007/s11661-004-0094-810.1007/s11661-004-0094-8 ↗
12. 10.1016/j.msea.2007.01.04610.1016/j.msea.2007.01.046 ↗
13. 10.1016/j.msea.2011.11.09210.1016/j.msea.2011.11.092 ↗
14. 10.1016/j.msea.2019.13844110.1016/j.msea.2019.138441 ↗
15. Processing AlSi10Mg by selective laser melting: Parameter optimisation and material characterisation10.1179/1743284714Y.0000000702 ↗
16. 10.1016/j.actamat.2015.05.01710.1016/j.actamat.2015.05.017 ↗
17. 10.1016/S0921-5093(03)00079-010.1016/S0921-5093(03)00079-0 ↗
18. 10.1016/j.jmst.2018.12.00610.1016/j.jmst.2018.12.006 ↗
19. 10.1016/j.msea.2007.05.07910.1016/j.msea.2007.05.079 ↗
20. 10.1016/j.jallcom.2018.04.05410.1016/j.jallcom.2018.04.054 ↗
21. 10.1073/pnas.040006610110.1073/pnas.0400066101 ↗
22. 10.1007/BF0241105910.1007/BF02411059 ↗
23. 10.1016/j.actamat.2018.09.05010.1016/j.actamat.2018.09.050 ↗
24. 10.1016/j.actamat.2017.03.06610.1016/j.actamat.2017.03.066 ↗
25. Influence of heat treatments on the microstructure and tensile behaviour of selective laser melting-produced TI-6AL-4V parts
26. 10.1016/j.scriptamat.2014.12.02310.1016/j.scriptamat.2014.12.023 ↗
27. 10.1016/j.actamat.2010.02.00410.1016/j.actamat.2010.02.004 ↗
28. 10.1557/mrs2010.56710.1557/mrs2010.567 ↗
29. 10.1038/nmat208510.1038/nmat2085 ↗
30. 10.1007/s11465-015-0341-210.1007/s11465-015-0341-2 ↗
31. 10.1016/j.jallcom.2018.03.33510.1016/j.jallcom.2018.03.335 ↗
32. 10.1038/nmat422810.1038/nmat4228 ↗
33. 10.1016/j.actamat.2017.11.05110.1016/j.actamat.2017.11.051 ↗
34. High-temperature mechanical properties of alloy 718 produced by laser powder bed fusion with different processing parameters
35. 10.1016/j.engfracmech.2019.03.04010.1016/j.engfracmech.2019.03.040 ↗
36. 10.3390/met1005062910.3390/met10050629 ↗
37. 10.1002/adem.20150015810.1002/adem.201500158 ↗
38. 10.1016/j.phpro.2016.08.08110.1016/j.phpro.2016.08.081 ↗
39. 10.1016/j.matdes.2011.09.05110.1016/j.matdes.2011.09.051 ↗
40. 10.1016/j.jallcom.2014.09.17710.1016/j.jallcom.2014.09.177 ↗
41. 10.1016/j.msea.2015.06.02110.1016/j.msea.2015.06.021 ↗
42. 10.1016/j.jallcom.2012.07.02210.1016/j.jallcom.2012.07.022 ↗
43. 10.1016/j.jmatprotec.2007.04.11710.1016/j.jmatprotec.2007.04.117 ↗
44. 10.1016/j.jallcom.2019.15261510.1016/j.jallcom.2019.152615 ↗
45. 10.1016/j.actamat.2011.12.03210.1016/j.actamat.2011.12.032 ↗
46. 10.1016/j.matlet.2015.10.13610.1016/j.matlet.2015.10.136 ↗
47. 10.1016/j.actamat.2016.07.01210.1016/j.actamat.2016.07.012 ↗
48. Microstructure evolution during in-situ heating of AlSi10Mg alloy powders and additive manufactured parts
49. 10.1016/j.scriptamat.2016.10.03510.1016/j.scriptamat.2016.10.035 ↗
50. 10.1016/j.jallcom.2017.10.28010.1016/j.jallcom.2017.10.280 ↗
51. 10.1016/j.matdes.2017.05.06510.1016/j.matdes.2017.05.065 ↗
52. 10.1016/j.msea.2020.14041510.1016/j.msea.2020.140415 ↗
53. 10.1038/nmat171410.1038/nmat1714 ↗
54. 10.1073/pnas.050654410210.1073/pnas.0506544102 ↗
55. 10.1016/j.msea.2019.13851110.1016/j.msea.2019.138511 ↗
56. 10.1063/1.496044310.1063/1.4960443 ↗
57. 10.1016/j.jallcom.2011.10.10710.1016/j.jallcom.2011.10.107 ↗
58. 10.1016/j.msea.2015.05.03510.1016/j.msea.2015.05.035 ↗
59. 10.1016/j.msea.2016.05.08910.1016/j.msea.2016.05.089 ↗
60. 10.1007/s12274-008-8008-510.1007/s12274-008-8008-5 ↗
61. 10.1016/j.matchar.2009.10.00310.1016/j.matchar.2009.10.003 ↗
62. 10.1557/mrs.2016.21410.1557/mrs.2016.214 ↗
63. 10.3390/met706019610.3390/met7060196 ↗
64. 10.1007/s11837-015-1793-x10.1007/s11837-015-1793-x ↗
65. 10.1021/nl201890s10.1021/nl201890s ↗
66. 10.1007/s11665-014-0958-z10.1007/s11665-014-0958-z ↗
67. 10.1016/j.msea.2017.02.06210.1016/j.msea.2017.02.062 ↗
68. 10.1007/s11837-015-1459-810.1007/s11837-015-1459-8 ↗