Large‐scale data principal component analysis of phase transition from a‐Si:H to nc‐Si:H using PECVD optical emission spectra
Source abstract
Abstract
Phase transformation of hydrogenated nanocrystalline silicon (nc‐Si:H) films was essential in the solar cells industry. Therefore, the plasma chemistry monitoring of in‐situ diagnostics optical emission spectroscopy (OES) of plasma‐enhanced chemical vapour deposition (PECVD) is deemed crucial for investigating the phase transformation. The proposed PC2‐OES algorithm can be used to monitor the PECVD process health condition of the crystallisation rate at different hydrogen dilution ratios. Principal component analysis (PCA) was performed to distinguish the crucial role of nc‐Si:H emission characteristics of plasma chemistry and the resultant crystallisation rate. Measurement results revealed that OES spectra characterisation confirmed that the crystallisation rate index (Hα*/SiH*) was highly correlated to hydrogen dilution ratio ( R ) and phase transformation of nc‐Si:H film. The proposed PCA‐based evaluation method will provide valuable information to reflect consistently the crystallisation rate of deposited films with different hydrogen dilution ratio and possibly other processing parameters of mass flow rate and applied power density.
Source: crossref · Quality: baseline
Research context
OpenAlex topics: Thin-Film Transistor Technologies · Silicon and Solar Cell Technologies · Silicon Nanostructures and Photoluminescence
SciVX discovery tags are terminology-based. OpenAlex topics are source-provided classifications.
Affiliations
Department of Mechanical Engineering National Central University No. 300, Zhongda Rd. Zhongli District Taoyuan Taiwan
Opto‐mechatronics Engineering National Central University No. 300, Zhongda Rd. Zhongli District Taoyuan Taiwan
References (30)
Show source-provided references
1. 10.1016/S0040‐6090(02)01203‐810.1016/S0040‐6090(02)01203‐8 ↗
2. 10.1063/1.11218310.1063/1.112183 ↗
3. 10.1016/S0022‐3093(99)00744‐910.1016/S0022‐3093(99)00744‐9 ↗
4. 10.1016/j.materresbull.2012.06.05110.1016/j.materresbull.2012.06.051 ↗
5. SchroppR.XuY.IwaniczkoE.et al.: ‘Microcrystalline silicon for solar cells at high deposition rates by hot wire cvd’.MRS Proc. 2002 715 A26.3. doi:10.1557/PROC-715-A26.3 ↗
6. KleinS.FingerF.CariusR.et al.: ‘High efficiency thin film solar cells with intrinsic microcrystalline silicon prepared by hot wire cvd’.MRS Proc. 2002 715 A26.2. doi:10.1557/PROC-715-A26.2 ↗
7. 10.1143/JJAP.39.L1910.1143/JJAP.39.L19 ↗
8. 10.1143/JJAP.37.L111610.1143/JJAP.37.L1116 ↗
9. 10.1016/S0040‐6090(01)01277‐910.1016/S0040‐6090(01)01277‐9 ↗
10. 10.1016/j.jnoncrysol.2017.08.03210.1016/j.jnoncrysol.2017.08.032 ↗
11. 10.1063/1.298751910.1063/1.2987519 ↗
12. 10.1088/0963‐0252/24/2/02501910.1088/0963‐0252/24/2/025019 ↗
13. 10.1063/1.34391510.1063/1.343915 ↗
14. 10.1063/1.279973810.1063/1.2799738 ↗
15. 10.1088/0963‐0252/16/1/01110.1088/0963‐0252/16/1/011 ↗
16. 10.1016/j.tsf.2009.02.05310.1016/j.tsf.2009.02.053 ↗
17. 10.3390/coatings807023810.3390/coatings8070238 ↗
18. 10.1016/S0257‐8972(03)00115‐410.1016/S0257‐8972(03)00115‐4 ↗
19. 10.1016/S0040‐6090(00)01677‐110.1016/S0040‐6090(00)01677‐1 ↗
20. 10.1088/0963‐0252/5/2/03310.1088/0963‐0252/5/2/033 ↗
21. 10.1016/j.mfglet.2013.09.00510.1016/j.mfglet.2013.09.005 ↗
22. 10.1016/j.renene.2016.08.01810.1016/j.renene.2016.08.018 ↗
23. 10.1016/j.renene.2012.02.01810.1016/j.renene.2012.02.018 ↗
24. 10.1007/978-1-4757-1904-810.1007/978-1-4757-1904-8 ↗
25. 10.1007/s00170‐018‐2938‐110.1007/s00170‐018‐2938‐1 ↗
26. 10.1080/0951192950894466410.1080/09511929508944664 ↗
27. 10.1016/0166‐3615(96)00013‐910.1016/0166‐3615(96)00013‐9 ↗
28. 10.1039/C4RA04610B10.1039/C4RA04610B ↗
29. 10.1016/j.matchemphys.2019.12218610.1016/j.matchemphys.2019.122186 ↗
30. 10.1063/1.35643210.1063/1.356432 ↗