Thermally induced oxidative growth of copper oxide nanowire on dendritic micropowder and reductive conversion to copper nanowire

Copper nanowires (NWs) were constructed on a dendritic copper powder precursor by a facile thermal oxidation–reduction method. First, copper oxide NWs were grown from high purity dendritic copper powder by thermal oxidation at 500°C. Next, these oxide NWs were reduced to copper NWs under a hydrogen flow at two different temperatures of 220 and 500°C. Oxide NW diameters distribution was in the range of 50–105 nm with length ranging from 1 to 5 µm while copper NWs were shorter and wider. A time‐dependent study of oxide NWs growth was carried out. The morphology, composition and crystal structure of the resulting products were characterised by X‐ray diffraction and scanning electron microscope. The results indicated that the final product of oxidation process was dispersed cupric oxide (CuO) NW whose density and length increased with time. Furthermore, it was observed that as the reduction temperature increased, the copper NW melted and adhered to the powder surface.