Grain refinement of micrometer-scale Cu foils through accumulative cyclic deformation
Source abstract
Abstract
The microstructure evolution of the 190 μ m-thick Cu foils subjected to repeatedly bending loading was investigated. We found that the grains in the micron-scale foil were refined into subgrains with a size of about 0.5 μ m through a removal of twin boundaries and an introduction of a high frequency of high angle boundaries (>15°) with accumulative cyclic deformation. With increasing strain rate (loading frequency), the grains are completely refined into well-defined fine grains with high angle boundaries. Such the microstructure refinement induced by accumulative cyclic deformation may provide a potential strategy for grain refinement of small-scale materials.
Source: openalex_inverted_index · Quality: baseline
Research context
OpenAlex topics: Microstructure and mechanical properties · High-Velocity Impact and Material Behavior · Surface Treatment and Residual Stress
SciVX discovery tags are terminology-based. OpenAlex topics are source-provided classifications.
References (37)
Show source-provided references
1. 10.1016/j.pmatsci.2006.02.00310.1016/j.pmatsci.2006.02.003 ↗
2. 10.1016/S0921-5093(00)01660-910.1016/S0921-5093(00)01660-9 ↗
3. 10.1016/j.actamat.2004.06.01710.1016/j.actamat.2004.06.017 ↗
4. 10.1016/j.scriptamat.2015.03.00610.1016/j.scriptamat.2015.03.006 ↗
5. 10.1016/j.pmatsci.2008.03.00210.1016/j.pmatsci.2008.03.002 ↗
6. 10.1016/S1359-6454(02)00466-410.1016/S1359-6454(02)00466-4 ↗
7. 10.1016/j.actamat.2006.07.01310.1016/j.actamat.2006.07.013 ↗
8. 10.1016/j.actamat.2004.05.02310.1016/j.actamat.2004.05.023 ↗
9. 10.1016/j.actamat.2006.08.01410.1016/j.actamat.2006.08.014 ↗
10. 10.1016/S1359-6454(98)00365-610.1016/S1359-6454(98)00365-6 ↗
11. 10.1016/S1359-6462(02)00282-810.1016/S1359-6462(02)00282-8 ↗
12. 10.1179/mst.1990.6.11.103910.1179/mst.1990.6.11.1039 ↗
13. 10.1016/0921-5093(89)90325-010.1016/0921-5093(89)90325-0 ↗
14. 10.1016/j.msea.2005.08.20110.1016/j.msea.2005.08.201 ↗
15. 10.1016/0956-7151(92)90296-Q10.1016/0956-7151(92)90296-Q ↗
16. 10.1016/0956-7151(94)90435-910.1016/0956-7151(94)90435-9 ↗
17. 10.1016/0001-6160(84)90145-710.1016/0001-6160(84)90145-7 ↗
18. 10.1179/174328408X38223510.1179/174328408X382235 ↗
19. 10.1016/j.matchar.2017.11.04610.1016/j.matchar.2017.11.046 ↗
20. 10.1016/0921-5093(89)90290-610.1016/0921-5093(89)90290-6 ↗
21. Courtney T · Mechanical Behavior of Materials · 2000
22. 10.1016/0167-6636(94)90054-X10.1016/0167-6636(94)90054-X ↗
23. 10.1016/S0167-6636(97)00036-710.1016/S0167-6636(97)00036-7 ↗
24. 10.1016/S0167-6636(02)00164-310.1016/S0167-6636(02)00164-3 ↗
25. 10.1063/1.170736310.1063/1.1707363 ↗
26. 10.1016/j.actamat.2007.01.00210.1016/j.actamat.2007.01.002 ↗
27. 10.1016/j.actamat.2008.10.02110.1016/j.actamat.2008.10.021 ↗
28. 10.1179/174328407X18580210.1179/174328407X185802 ↗
29. 10.1016/j.ijfatigue.2017.03.03710.1016/j.ijfatigue.2017.03.037 ↗
30. 10.1016/j.ijfatigue.2015.11.02910.1016/j.ijfatigue.2015.11.029 ↗
31. 10.1016/j.scriptamat.2012.07.04910.1016/j.scriptamat.2012.07.049 ↗
32. 10.1080/1478643700823842610.1080/14786437008238426 ↗
33. 10.1073/pnas.132406911110.1073/pnas.1324069111 ↗
34. 10.1016/j.actamat.2016.06.02310.1016/j.actamat.2016.06.023 ↗
35. 10.1016/S0022-5096(97)00086-010.1016/S0022-5096(97)00086-0 ↗
36. 10.1016/j.actamat.2009.11.03110.1016/j.actamat.2009.11.031 ↗
37. 10.1016/j.actamat.2015.06.05110.1016/j.actamat.2015.06.051 ↗