Thermal stability, optical and Photoluminescence properties of spherical Ce _x Zr_1−x O₂ (x = 0.05) crystalline blue-emitting nanophosphors synthesized by microwave method

Nanocrystalline ZrO2 based material is an impressive candidate for the various functional applications owing to their ease of preparation and high thermal stability. This paper reports the synthesis, structural and optical characterization of thermally stable monodispersed CexZr1−xO2 (x = 0.05) nanoparticles. This method is based on the fact that, microwave irradiation allows the formation of size controlled and single phase cubic ZrO2 nanoparticles containing Ce+4 as a dopant. The XRD and Rietveld analysis revealed the formation of the crystalline cubic fluorite phase. The formation of nanoparticles was confirmed by FTIR. The morphology of the nanophosphors was characterised by FESEM and TEM. The optical band gap was calculated from the UV–visible absorption spectra and was found to vary from 3.93 to 4.25 eV with calcination temperature. It shows the decrease in the optical band gap from the pristine ZrO2. The particle size was measured by using HRTEM, and the average particle size was found to be 22 nm. Under the 268 nm Ultra Violet irradiation excitation a blue emission at 443 nm was observed at room temperature. The possible luminescence mechanism of CexZr1−xO2 nanophosphor under UV excitation is discussed.