Effect of modified mold shell on the microstructure and tensile fracture morphology of single-crystal nickel-base superalloy

Weitai Xu, Yutao Zhao, Shaochun Sun, Manping Liu, Dexin Ma, Xiangfeng Liang, Cunlong Wang, Ran Tao

Materials Research Express· Volume 5· Issue 4
Publisher page

Abstract

The mold shell used for single-crystal turbine blades preparation was modified from conventional process to fiber reinforcement technology. The wall thickness was decreased by 32.3 percent (pct) than the conventional process. Then these two mold shells were used to produce single crystal samples of nickel-base superalloy in a Bridgman furnace. The local temperature curves were recorded in the process. The results show that the modified mold shell can increase the temperature gradient in the mushy zone than the conventional mold shell. The primary and secondary dendrite arm space were reduced by 8 pct and 12 pct, respectively. Moreover, both the area fraction and mean size of the γ'/γ eutectic were declined, as well as the dendritic segregation tendency. Therefore it contributed to the lower residual eutectic and micro-porosity in the heat-treated microstructure. Further, fracture surface of the samples made by modified mold shell exhibited smaller facets and more uniform dimples in the size and shape.
Source: openalex_inverted_index · Quality: baseline

Research context

OpenAlex topics: High Temperature Alloys and Creep · Aluminum Alloy Microstructure Properties · High-Temperature Coating Behaviors

SciVX discovery tags are terminology-based. OpenAlex topics are source-provided classifications.

References (25)

Show source-provided references
1. 10.1016/j.matchar.2015.01.00310.1016/j.matchar.2015.01.003 ↗
2. 10.1016/j.msea.2007.05.08010.1016/j.msea.2007.05.080 ↗
3. 10.1007/s11837-003-0156-110.1007/s11837-003-0156-1 ↗
4. Fu H Z · Sci. Technol. Adv. Mater. · 2001 · 2 · 19710.1016/S1468-6996(01)00049-3 ↗
5. Lu Z L · P. I. Mech. Eng. B-J. Eng. · 2014 · 228 · 695
6. 10.1007/s11661-016-3415-910.1007/s11661-016-3415-9 ↗
7. 10.1007/s11661-003-0229-310.1007/s11661-003-0229-3 ↗
8. Zhang Y · J. Mater. Eng. · 1997 · 5 · 31
9. Yao J · Rare Metal Mater. Eng. · 2009 · 38 · 1222
10. 10.4028/www.scientific.net/AMM.492.39210.4028/www.scientific.net/AMM.492.392 ↗
11. 10.1007/s11663-004-0013-910.1007/s11663-004-0013-9 ↗
12. 10.1007/s11663-015-0461-410.1007/s11663-015-0461-4 ↗
13. Xu K · 2016
14. 10.1016/j.actamat.2014.05.04010.1016/j.actamat.2014.05.040 ↗
15. 10.1016/j.applthermaleng.2015.10.07310.1016/j.applthermaleng.2015.10.073 ↗
16. 10.1016/j.ceramint.2014.03.16310.1016/j.ceramint.2014.03.163 ↗
17. 10.1016/j.jcrysgro.2003.08.07110.1016/j.jcrysgro.2003.08.071 ↗
18. 10.1016/j.actamat.2009.08.01310.1016/j.actamat.2009.08.013 ↗
19. 10.1007/s11661-011-0664-510.1007/s11661-011-0664-5 ↗
20. 10.1007/s12613-016-1281-510.1007/s12613-016-1281-5 ↗
21. 10.1016/0025-5416(83)90199-410.1016/0025-5416(83)90199-4 ↗
22. 10.1007/BF0077866610.1007/BF00778666 ↗
23. 10.1016/j.msea.2015.07.04510.1016/j.msea.2015.07.045 ↗
24. 10.1007/s10853-015-9524-910.1007/s10853-015-9524-9 ↗
25. Ma S Y · Mater. Res. Express · 2017 · 4