Preparation of the rod-like β-Si3N4 particles favoring the self-reinforcing Si3N4 ceramics

Abstract The β-Si 3 N 4 particles were prepared by heating original α-Si 3 N 4 powder with rare earth oxide Nd 2 O 3 or Yb 2 O 3 additives at 1600–1700 °C for 1.5 h. The transformation ratio of α-Si 3 N 4 was also investigated by XRD. The results showed that Yb 2 O 3 could accelerate the transformation of Si 3 N 4 more effectively than Nd 2 O 3 and the powder heated at 1700 °C with over 4 wt.% Yb 2 O 3 has a high transformation ratio of over 98%. The morphologies of the heated powders were observed by scanning electron microscopy. The results showed that the powder heated at 1700 °C with 4 wt.% Yb 2 O 3 had ideal β-Si 3 N 4 rod-like morphology particles. This heated powder was used as a seed by adding it to the original α-Si 3 N 4 powder to prepare self-reinforced Si 3 N 4 ceramic by hot-pressed sintering. The fracture toughness of the seeded Si 3 N 4 ceramics increased to 9.1 MPa m 1/2 from 7.6 MPa m 1/2 of the unseeded Si 3 N 4 ceramics, while the high value of strength was still kept at 1200 °C.