Microwave dielectric characteristics of Mg(Ta1−xNbx)2O6 ceramics

Abstract The crystalline phase and the microwave dielectric properties of the Mg(Ta 1− x Nb x ) 2 O 6 ceramics have been investigated. Combining the positive temperature coefficient of the resonant frequency ( τ f ) material (MgTa 2 O 6 , τ f = +30 ppm/°C) with the negative one (MgNb 2 O 6 , τ f = −70 ppm/°C) can produce the composite with τ f ∼ 0 ppm/°C. The crystal structure of pure MgTa 2 O 6 ceramic is the tetragonal structure. For x = 0.15, the crystal structure of the solid solution was the coexistence of the tetragonal structure and orthorhombic structure. Solid solutions with 0.25 ≦ x ≦ 1 exhibit the orthorhombic structure, which is like the structure of pure MgNb 2 O 6 ceramic. The sintered morphologies of Mg(Ta 1− x Nb x ) 2 O 6 ceramics gradually change from the disk-typed grains ( x = 0 and 0.15) to the disk-typed and bar-typed grains coexist ( x = 0.35, 0.5, and 0.7), and then reveal the bar-typed grains ( x = 0.85 and 1). The densities, dielectric constants ( ɛ r ) and τ f values of Mg(Ta 1− x Nb x ) 2 O 6 ceramics decrease with the increase of the MgNb 2 O 6 content. The quality factor ( Q × f ) reaches the minimum value at x = 0.15, and then increases with the increase of the MgNb 2 O 6 content. The Mg(Ta 1− x Nb x ) 2 O 6 ceramic with x = 0.25 sintered at 1450 °C exhibits a minimum τ f value of −0.7 ppm/°C.