Hydrothermal synthesis and luminescent properties of LaPO4:Eu 3D microstructures with controllable phase and morphology

Abstract Three types of Eu 3+ -doped LaPO 4 three-dimensional (3D) microstructures have been hydrothermally prepared by adjusting pH value and the molar ratio of La 3+ and Eu 3+ to phosphorus of Na 5 P 3 O 10 (Ln/P) at 180 °C. As the pH value was 0.15 and the molar ratio of Ln/P was in the range of 1/1 to 1/4, 5 μm urchinlike spheres composed of long nanorods of hexagonal LaPO 4 :Eu were obtained. As the pH value was 1.00 and the molar ratio of Ln/P was 1/1, 3 μm hollow spheres consisting of short nanorods of monoclinic LaPO 4 :Eu were prepared. Keeping the pH value at 1.0 and the molar ratio of Ln/P at 1/4, 6 μm core–shell spheres of monoclinic LaPO 4 :Eu formed. Luminescent measurements were performed. Hollow spheres of monoclinic LaPO 4 :Eu had the strongest emission intensity. However, the emission intensity of monoclinic core/shell structure was even lower than that of hexagonal LaPO 4 :Eu urchinlike spheres.