Neutron structural characterization, inversion degree and transport properties of NiMn2O4 spinel prepared by the hydroxide route

Abstract The title compound has been synthesized by the hydroxide route. The crystal structure has been investigated at room temperature from high-resolution neutron powder diffraction (NPD) data. It crystallizes in a cubic spinel structure, space group F d 3 ¯ m , Z = 8, with a = 8.3940(2) A at 295 K. The crystallographic formula is (Ni 0.202(1) Mn 0.798(1) ) 8a (Ni 0.790(1) Mn 1.210(1) ) 16d O 4 where 8 a and 16 d stand for the tetrahedral and octahedral sites of the spinel structure, respectively. There is a significant inversion degree of the spinel structure, λ = 0.80. In fact, the variable parameter for the oxygen position, u = 0.2636(4), is far from that expected ( u = 0.25) for normal spinels. From a bond-valence study, it seems that the valence distribution in NiMn 2 O 4 spinel is not as trivial as expected (Ni 2+ and Mn 3+ ), but clearly the tetrahedral Mn ions are divalent whereas the octahedral Mn and Ni are slightly oxidized from the expected +3 and +2 values, respectively. The mixed valence observed at the octahedral sites provides the charge carriers that, by a hopping mechanism between Mn 3+ /Mn 4+ adjacent sites, leads to a significant conductivity, up to 0.85 S cm −1 at 800 °C in air.