Characterization and catalytic properties of Ni/SiO2 catalysts prepared with nickel citrate as precursor

Abstract The Ni/SiO 2 catalysts were prepared with nickel citrate precursor by using incipient-wetness impregnation method, characterized by FT-IR, UV-Raman, TG-DTA, XRD, HR-TEM and H 2 -TPR, and tested in the reaction of methane reforming with CO 2 and O 2 to produce syngas. The highly-dispersed Ni particles (∼7 nm) on support SiO 2 were observed by TEM. FT-IR results indicated that there existed interaction between nickel citrate precursor and SiO 2 . H 2 -TPR results demonstrated that, this interaction was enhanced by calcination at high temperature to form strong NiO–SiO 2 interaction, and the strong interaction was recovered after repeating oxidation–reduction–oxidation cycle at 700 °C. As a result, the Ni/SiO 2 catalysts showed a good activity and super stability without sintering of nickel particles during 36 h reaction on stream.