Effect of aluminum source on the synthesis of AlN powders from combustion synthesis precursors
Source abstract
Abstract
Abstract In the present work, the carbothermal reduction method was employed to fabricate the AlN powders by utilizing the combustion synthesized precursor derived from the mixed solution comprised of an aluminum source (Al(NO 3 ) 3 or Al 2 (SO 4 ) 3 or AlCl 3 ), glucose, nitric acid, and urea. Effects of aluminum source on the particle size and morphology of precursors as well as synthesized AlN powders were studied in detail. The size and morphology of precursors, derived from various aluminum sources, had exhibited significant differences. The precursor from Al(NO 3 ) 3 source had completed the nitridation reaction at 1500 °C in 2 h. However, the nitridation reactions of the precursors from Al 2 (SO 4 ) 3 or AlCl 3 source furnished at increased temperature of 1550 °C in 2 h. Moreover, the AlN powders from various aluminum sources have been synthesized directly from γ-Al 2 O 3 without γ-Al 2 O 3 to α-Al 2 O 3 phase transition. The AlN powders from Al(NO 3 ) 3 , calcined at 1550 °C for 2 h, were comprised of well-distributed spherical particles with an average size of 80 nm. While the AlN powders from AlCl 3 or Al 2 (SO 4 ) 3 consisted of heterogeneously distributed spherical particles ranging from 100 to 200 nm or from 80 to 150 nm, respectively.
Source: openaire · Quality: candidate unverified · Source record ↗
Research context
OpenAlex topics: Advanced ceramic materials synthesis · Magnesium Oxide Properties and Applications · Aluminum Alloys Composites Properties
SciVX discovery tags are terminology-based. OpenAlex topics are source-provided classifications.
References (20)
Show source-provided references
1. Sheppard · Am. Ceram. Soc. Bull. · 1990 · 69 · 1801
2. Mussler · Am. Ceram. Soc. Bull. · 2000 · 79 · 45
3. Selvaduray · Mater. Sci. Technol. · 1993 · 9 · 46310.1179/026708393790172196 ↗
4. Lefort · J. Am. Ceram. Soc. · 1993 · 76 · 229510.1111/j.1151-2916.1993.tb07767.x ↗
5. Silverman · Adv. Ceram. Mater. · 1988 · 3 · 41810.1111/j.1551-2916.1988.tb00248.x ↗
6. Jung · J. Mater. Chem. · 1994 · 4 · 94910.1039/jm9940400949 ↗
7. Hashimoto · J. Am. Ceram. Soc. · 1991 · 74 · 128210.1111/j.1151-2916.1991.tb04098.x ↗
8. Kroke · J. Am. Ceram. Soc. · 2002 · 85 · 311710.1111/j.1151-2916.2002.tb00595.x ↗
9. Pathak · J. Am. Ceram. Soc. · 1999 · 82 · 25710.1111/j.1151-2916.1999.tb01757.x ↗
10. Suehiro · J. Am. Ceram. Soc. · 2003 · 86 · 104610.1111/j.1151-2916.2003.tb03420.x ↗
11. Yamakawa · J. Eur. Ceram. Soc. · 2006 · 26 · 241310.1016/j.jeurceramsoc.2005.04.030 ↗
12. Tseng · J. Mater. Sci. · 1996 · 31 · 355910.1007/BF00360762 ↗
13. Jung · J. Eur. Ceram. Soc. · 2001 · 21 · 7910.1016/S0955-2219(00)00173-4 ↗
14. Kingsley · Mater. Lett. · 1988 · 11–12 · 42710.1016/0167-577X(88)90045-6 ↗
15. Qin · J. Eur. Ceram. Soc. · 2009 · 29 · 79510.1016/j.jeurceramsoc.2008.07.019 ↗
16. Qin · Mater. Res. Bull. · 2008 · 43 · 295410.1016/j.materresbull.2007.12.008 ↗
17. Ramanathan · Ceram. Int. · 1997 · 23 · 4510.1016/0272-8842(95)00139-5 ↗
18. Hashimoto · J. Jpn. Ceram. Soc. · 1991 · 99 · 75110.2109/jcersj.99.751 ↗
19. Bachelard · Mater. Sci. Eng. A · 1989 · 109 · 24710.1016/0921-5093(89)90595-9 ↗
20. Cho · Mater. Sci. Technol. · 1991 · 7 · 49510.1179/mst.1991.7.6.495 ↗