Novel hydrothermal synthesis method for tobermorite fibers and investigation on their thermal stability
Source abstract
Abstract
Abstract Tobermorite fibers have been successfully synthesized by hydrothermal reaction at 200°C under the pressure of 2 MPa after 3–10 h using a Ca(II)–EDTA complex precursor. XRD patterns, TG-DTA analysis, and SEM observations show that the products are needle-like tobermorite fibers, which have diameter, length, and aspect ratio in the range of 0.1–10, 40–100, and 20–80 μm, respectively. The fibers can maintain their shapes up to 1150°C during the heat treatment.
Source: openaire · Quality: candidate unverified · Source record ↗
Research context
OpenAlex topics: Natural Fiber Reinforced Composites · Advanced Cellulose Research Studies · Electrospun Nanofibers in Biomedical Applications
SciVX discovery tags are terminology-based. OpenAlex topics are source-provided classifications.
References (19)
Show source-provided references
1. Tobermorite and calcium silicate products
2. Xonotlite heat-insulating material with bulk density of 0.1
3. Hydrothermal reaction and industry of calcium silicate
4. T. Mitsuda, T. Saitou, E. Hattori, in: Proceedings of the First International Symposium on Hydrothermal Reactions, Yokohama (Gakujutsu Bunkenn Fukyu-kai, Tokyo, 1983), 22–26 March 1982, p. 823.
5. Structural form of spherical secondary particles of calcium silicate hydrate crystals and mechanical strength of the molded product
6. Fibrous calcium silicates
7. Effect of silica raw materials on the texture of synthesized xonotlite
8. Effect of raw lime materials on the textures of synthesized xonotlite
9. Crystal shape and size controls of xonotlite
10. Experimental studies on xonotlite in the SiO2–CaO–H2O system: with special reference to the spherical secondary particles
11. Direct formation of xonotlite fiber with continuous-type autoclave
12. Hydrothermal synthesis of xonotlite whiskers by ion diffusion10.1023/A:1018575702546 ↗
13. Hydrothermal synthesis of needle-like barium using a barium(II)-EDTA chelate precursor and sulfate ions10.1023/A:1006761401595 ↗
14. Monodispersed metal (hydrous) oxides—a fascinating field of colloid science10.1021/ar00061a004 ↗
15. Substitutions in apatite: I. Potassium-bearing apatite
16. Hydrothermal synthesis of biocompatible whiskers10.1007/BF00352039 ↗
17. Biocompatible whiskers with controlled morphology and stoichiometry10.1557/JMR.1995.0521 ↗
18. Texture and formation mechanism of fibrous calcium hydroxyapatite particles prepared by decomposition of calcium–EDTA chelates10.1111/j.1151-2916.1997.tb02958.x ↗
19. Synthetic wollastonite and molded material from it