Synthesis of BaTi4O9 ceramics by reaction-sintering process

Abstract Synthesis of BaTi 4 O 9 ceramics by a reaction-sintering process was investigated. The mixture of raw materials for stoichiometric BaTi 4 O 9 were pressed and sintered into ceramics without any calcination stage involved. Pure BaTi 4 O 9 phases were obtained at 1150–1280 °C. High-sintered density, 98.2–99.5% of theoretical value (4.533 g/cm 3 ), can be obtained for pellets sintered at 1200–1280 °C for 2–6 h. Some rod-shaped grains 3–7 μm in the longitudinal axis appear in pellets sintered at 1230 °C. Both the size and the amount of these rod-shaped grains increase at higher sintering temperature.