Dopant occupancy and increased exposure energy of Zr:Yb:Ho:LiNbO3 crystals

Abstract Yb:Ho:LiNbO 3 crystals tridoped with various Zr 4+ concentrations (0, 1, 2 and 5 mol%) were grown by Czochraski technique. Defect structure and dopant occupancy of Zr:Yb:Ho:LiNbO 3 crystals were determined by IR transmission spectrum. The effective distribution coefficient of Zr ion increases with increasing ZrO 2 concentration in the melts, which is near to one. The light-induced scattering of Zr:Yb:Ho:LiNbO 3 crystals was quantitatively measured via the incident exposure energy. The exposure energy of Zr (5 mol%):Yb:Ho:LiNbO 3 crystal is 49.33 J/cm 2 , which is two orders higher than that of Yb:Ho:LiNbO 3 crystal in magnitude. The photoconductivity is key factor to understand the internal relationship between the dopant occupancy and exposure energy of the crystals.