The effect of grain surface on the long afterglow properties of Sr 2 MgSi 2 O 7 : Eu 2+ , Dy 3+
Source abstract
Abstract
Abstract Sr2MgSi2O7: Eu2+, Dy3+ was chosen for the investigation about the effect of grain surface on the long afterglow properties. Three pulverizing ways (manual grinding, ball milling and roller milling) were carried out to obtain different grain surface morphologies of particles. The most grains of the luminous powders obtained by roller milling are intact, while those obtained by ball milling are tattered with the grains surface destroyed. As for manual grinding, part of the grains surface are destroyed. The initial luminescent intensity of the phosphor pulverized by roller milling is nearly twice of that prepared by ball milling. After ball milling, the pulverized phosphor is sintered once again at 1000 °C in reducing atmosphere. It follows that the luminescence properties are enhanced significantly with the opposite variation trend compared with that prepared by roller milling. This is closely related to the change of defect density on the grain surface of these phosphors.
Source: openaire · Quality: candidate unverified · Source record ↗
Research context
OpenAlex topics: Luminescence Properties of Advanced Materials · Radiation Detection and Scintillator Technologies · Glass properties and applications
SciVX discovery tags are terminology-based. OpenAlex topics are source-provided classifications.
References (30)
Show source-provided references
1. Investigation of persistent luminescence property of Bi3+, Dy3+ co-doped CdSiO3 phosphor10.1016/j.materresbull.2014.09.049 ↗
2. Fabrication and properties of Sr2MgSi2O7: Eu2+ Dy3+ nanostructures by an AAO template assisted co-deposition method10.1016/j.jallcom.2008.10.085 ↗
3. Effect of retrapping on the persistent luminescence in strontium silicate orange–yellow phosphor10.1016/j.jssc.2013.07.037 ↗
4. Afterglow phosphor materials Y2O2S: Eu, Mg, Ti doped with various Gd concentrations10.1016/j.jallcom.2010.04.139 ↗
5. Long afterglow properties of Eu2+/Mn2+ doped Zn2GeO410.1016/j.jlumin.2013.09.011 ↗
6. A red-emitting long-afterglow phosphor of Eu3+, Ho3+ co-doped Y2O310.1016/j.jallcom.2014.09.092 ↗
7. Investigation on the enhancement and the suppression of persistent luminescence of Re3+ doped Sr2EuMgSi2O7 (Re=Dy, Yb)10.1016/j.jallcom.2011.01.051 ↗
8. X-ray absorption study of rare earth ions in Sr2MgSi2O7: Eu2+, R3+ persistent luminescence materials, Opt10.1016/j.optmat.2008.12.020 ↗
9. Direct view of stress distribution in solid by mechanoluminescence10.1063/1.123865 ↗
10. The temperature dependence of luminescence from a long-lasting phosphor exposed to ionizing radiation10.1016/S0168-9002(01)00922-6 ↗
11. Nanoprobes with near-infrared persistent luminescence for in vivo imaging10.1073/pnas.0702427104 ↗
12. Enhanced luminescent properties of long-persistent Sr2MgSi2O7:Eu2+, Dy3+ phosphor prepared by the co-precipitation method10.1016/j.jlumin.2008.06.009 ↗
13. Preparation of long-afterglow colloidal solution of Sr2MgSi2O7: Eu2+, Dy3+ by laser ablation in liquid10.1016/j.apsusc.2010.09.067 ↗
14. Synthesis of Sr4Al14O25: Eu2+, Dy3+ phosphor nanometer powders by combustion processes and its optical properties10.1016/j.mseb.2006.06.042 ↗
15. Processing fine powders by roll press10.1016/j.powtec.2014.07.046 ↗
16. A specific energy-based size reduction model for batch grinding ball mill10.1016/j.mineng.2014.09.006 ↗
17. Influence on the long afterglow properties by the environmental temperature10.1016/j.jlumin.2009.07.031 ↗
18. Blue long lasting phosphorescence of Tm3+ in zinc pyrophosphate phosphor10.1016/j.jallcom.2008.03.104 ↗
19. Luminescence studies on the blue–green emitting Sr4Al14O25: Ce3+ phosphor synthesized through solution combustion route10.1016/j.jlumin.2008.09.002 ↗
20. Chung · 2008
21. Optical energy storage properties of Sr2MgSi2O7: Eu2+, R3+ persistent luminescence materials10.1007/s10973-011-1403-2 ↗
22. Isolated defects in Sr2MgSi2O7: a DFT study10.1016/j.phpro.2012.03.701 ↗
23. Influence on the luminescence properties of the lattice defects in Sr2MgSi2O7: Eu2+, M(M=Dy3+, La3+ or Na1+)10.1016/j.jallcom.2010.03.060 ↗
24. Role of defect states in persistent luminescence materials10.1016/j.jallcom.2003.11.064 ↗
25. Charge creation, trapping, and long phosphorescence in Sr2MgSi2O7: Eu2+, RE3+10.1063/1.2844473 ↗
26. Long lasting phosphorescence in oxygen-deficient zinc–boron-germanosilicate glass–ceramics10.1016/j.jallcom.2010.05.080 ↗
27. Optical properties of SrAl2O4: Eu2+ phosphor in glass10.1016/j.optmat.2014.10.055 ↗
28. Electronic structure of defects in Sr2MgSi2O7: Eu2+, La3+ persistent luminescence material10.1016/j.jnoncrysol.2010.06.035 ↗
29. The structural properties of synthetic Sr-åkermanite, Sr2MgSi2O710.1524/zkri.1983.163.3-4.295 ↗
30. Synthesis of Sr2MgSi2O7: Eu, Dy and Sr2MgSi2O7: Eu, Dy, Nd by a modified solid-state reaction and their luminescent properties10.1016/j.jallcom.2007.04.261 ↗