Solvothermal synthesis of V4O9 flake-like morphology and its photocatalytic application in the degradation of methylene blue
Source abstract
Abstract
Abstract Flake-like nanocrystalline V4O9 has been successfully synthesized by solvothermal process using V2O5 as vanadium source and phenolphthalein as a reducing agent and a structure-directing template. Techniques X-ray diffraction (XRD), scanning electron microscopy (SEM), Fourier transform infrared (FTIR) spectroscopy and ultraviolet–visible (UV–vis) spectroscopy have been used to characterize the structure, the morphology and the composition of the material. The photocatalytic activity of the material has been evaluated by the degradation of methylene blue under visible light irradiation. As a result, after the lapse of 150 min, around 93.54% bleaching was observed, with V4O9 nanoflakes yielding more photodegradation compared to that of bulk V2O5. This presents a degradation percentage of about 44.67%.
Source: openaire · Quality: candidate unverified · Source record ↗
Research context
OpenAlex topics: Transition Metal Oxide Nanomaterials · Catalysis and Oxidation Reactions · Catalytic Processes in Materials Science
SciVX discovery tags are terminology-based. OpenAlex topics are source-provided classifications.
References (62)
Show source-provided references
1. Wang · Chem. Mater. · 2006 · 18 · 278710.1021/cm052765h ↗
2. Crespilho · Int. J. Electrochem. Sci. · 2006 · 1 · 19410.1016/S1452-3981(23)17150-1 ↗
3. Braithwaite · Chem. Mater. · 1999 · 11 · 199010.1021/cm980735r ↗
4. Dai · Chem. Mater. · 1999 · 11 · 308610.1021/cm9901461 ↗
5. Spahr · J. Electrochem. Soc. · 1999 · 146 · 278010.1149/1.1392008 ↗
6. Zhou · Chem. Lett. · 2007 · 36 · 31010.1246/cl.2007.310 ↗
7. Bond · Appl. Catal. · 1991 · 71 · 110.1016/0166-9834(91)85002-D ↗
8. Mamedov · Appl. Catal. A · 1995 · 127 · 110.1016/0926-860X(95)00056-9 ↗
9. Krusin-Elbaum · Nature · 2004 · 431 · 67210.1038/nature02970 ↗
10. Chen · J. Mater. Chem. · 2002 · 12 · 192610.1039/b203056j ↗
11. Chen · Mater. Res. Bull. · 2007 · 42 · 35410.1016/j.materresbull.2006.05.026 ↗
12. Haber · Appl. Catal. A · 1997 · 157 · 310.1016/S0926-860X(97)00017-3 ↗
13. Zavalij · Acta Crystallogr. B · 1999 · 55 · 62710.1107/S0108768199004000 ↗
14. Chirayil · Chem. Mater. · 1998 · 1 · 262
15. Manno · J. Non-Cryst. Solids · 2004 · 341 · 6810.1016/j.jnoncrysol.2004.04.020 ↗
16. Briand · J. Phys. Chem. · 2004 · 108B · 482310.1021/jp037675j ↗
17. Manning · J. Mater. Chem. · 2002 · 12 · 293610.1039/b205427m ↗
18. Xu · J. Mater. Sci. · 2004 · 3 · 48910.1023/B:JMSC.0000011503.22893.f4 ↗
19. Andersson · J. Catal. · 1986 · 98 · 20410.1016/0021-9517(86)90309-X ↗
20. Ozkan · Stud. Surf. Sci. Catal. · 1997 · 110 · 47110.1016/S0167-2991(97)81008-7 ↗
21. Tong · J. Mol. Catal. A · 2007 · 268 · 12010.1016/j.molcata.2006.12.013 ↗
22. Soriano · Appl. Catal. B · 2009 · 92 · 27110.1016/j.apcatb.2009.08.002 ↗
23. Bielański · Catal. Rev. Sci. Eng. · 1979 · 19 · 110.1080/03602457908065099 ↗
24. Wachs · J. Catal. · 1996 · 161 · 21110.1006/jcat.1996.0179 ↗
25. Niederberger · Chem. Mater. · 2000 · 12 · 199510.1021/cm001028c ↗
26. Livage · Chem. Mater. · 1991 · 3 · 57810.1021/cm00016a006 ↗
27. Spahr · Angew. Chem. Int. Ed. · 1998 · 37 · 126310.1002/(SICI)1521-3773(19980518)37:9<1263::AID-ANIE1263>3.0.CO;2-R ↗
28. Kam · Mater. Res. Bull. · 2006 · 41 · 101510.1016/j.materresbull.2006.03.024 ↗
29. Whittingham · Chem. Rev. · 2004 · 104 · 427110.1021/cr020731c ↗
30. Chen · Solid State Ionics · 2008 · 178 · 167610.1016/j.ssi.2007.10.015 ↗
31. Chirayil · Chem. Mater. · 1998 · 1 · 262910.1021/cm980242m ↗
32. Chine · Mater. Lett. · 2012 · 71 · 10110.1016/j.matlet.2011.12.049 ↗
33. Sediri · J. Solid State Chem. · 2002 · 167 · 40710.1016/S0022-4596(02)99633-7 ↗
34. Sediri · Ann. Chim. Sci. Mater. · 2003 · 28 · 12910.1016/S0151-9107(03)00011-4 ↗
35. Sediri · Mater. Lett. · 2009 · 63 · 1510.1016/j.matlet.2008.08.022 ↗
36. Sediri · J. Phys. Chem. Solids · 2007 · 68 · 182110.1016/j.jpcs.2007.06.012 ↗
37. Tudo · C. R. Acad. Sci. Paris · 1965 · 261 · 2911
38. Toda · Nippon Kagaku Zasshi · 1966 · 87 · 131110.1246/nikkashi1948.87.12_1311 ↗
39. Endo · Chem. Lett. · 1974 · 3 · 90510.1246/cl.1974.905 ↗
40. Theobald · C. R. Acad. Sci. Paris · 1969 · 26 · 1209
41. Wilhelmi · Acta Chem. Scand. · 1970 · 24 · 340910.3891/acta.chem.scand.24-3409 ↗
42. Sata · Kogyo Kagaku Zasshi · 1968 · 71 · 64310.1246/nikkashi1898.71.5_643 ↗
43. Sata · Kogyo Kagaku Zasshi · 1968 · 71 · 64710.1246/nikkashi1898.71.5_647 ↗
44. Sata · Bull. Tokyo Inst. Technol. · 1970 · 98 · 1
45. Yamazaki · J. Solid State Chem. · 2010 · 183 · 149610.1016/j.jssc.2010.04.007 ↗
46. Miyake · Appl. Catal. · 1995 · 131 · 4310.1016/0926-860X(95)00135-2 ↗
47. Théobald · C. R. Acad. Sci. · 1968 · C266 · 1534
48. Huang · Adv. Powder Technol. · 2012 · 23 · 21110.1016/j.apt.2011.02.009 ↗
49. Pavasupree · J. Solid State Chem. · 2005 · 178 · 215210.1016/j.jssc.2005.03.034 ↗
50. Subba Reddy · Electrochem. Commun. · 2006 · 8 · 27910.1016/j.elecom.2005.11.025 ↗
51. Naydenov · Micropor. Mesopor. Mater. · 2002 · 55 · 25310.1016/S1387-1811(02)00427-4 ↗
52. Blasco · J. Catal. · 1995 · 152 · 110.1006/jcat.1995.1054 ↗
53. Ding · J. Phys. Chem. B · 2001 · 105 · 392810.1021/jp003413v ↗
54. Ruh · Hazard. Mater. · 2008 · 156 · 19410.1016/j.jhazmat.2007.12.033 ↗
55. Zhou · J. Phys. Chem. C · 2007 · 111 · 1365910.1021/jp065155t ↗
56. Zhang · J. Mater. Chem. · 2007 · 17 · 252610.1039/b616460a ↗
57. Zhang · Small · 2007 · 3 · 161810.1002/smll.200700043 ↗
58. Zhou · Sep. Purif. Technol. · 2011 · 77 · 27510.1016/j.seppur.2010.12.017 ↗
59. Katafias · React. Kinet. Mech. Catal. · 2010 · 101 · 25110.1007/s11144-010-0234-7 ↗
60. Houas · Appl. Catal. B · 2001 · 31 · 14510.1016/S0926-3373(00)00276-9 ↗
61. Lizama · Catal. Today · 2002 · 76 · 23510.1016/S0920-5861(02)00222-5 ↗
62. Rajeshwar · J. Photochem. Photobiol. C · 2008 · 9 · 1510.1016/j.jphotochemrev.2008.09.001 ↗