Combustion synthesis and luminescence properties of yellow-emitting phosphors Ca2BO3Cl:Eu2+

Abstract Yellow-emitting phosphor Ca2BO3Cl:Eu2+ was synthesized by a solution-combustion method. The phase structure and microstructure were determined by the X-ray diffraction (XRD) and scanning electron microscope (SEM) analysis, respectively. The as-prepared Ca2BO3Cl:Eu2+ phosphor absorbed near ultraviolet and blue light of 320–500 nm, and showed an intense yellow emission band centered at 569 nm with the CIE coordinate of (0.453, 0.526). The lifetime of Eu2+ ions in Ca2BO3Cl:Eu2+ phosphor was measured, furthermore the temperature dependent luminescence property and mechanism were studied, which also testified that the present phosphor had a promising potential for white light-emitting diodes.