Synthesis of mesoporous hydroxyapatite using a modified hard-templating route

Mesoporous polycrystals of hydroxyapatite-calcium are synthesized via a modified hard-templating route. The structure properties of hydroxyapatite-calcium are characterized by means of X-ray diffraction, Fourier transform infrared spectroscopy, transmission electron microscopy and N{sub 2} adsorption-desorption isotherms. Wide-angle X-ray diffraction and Fourier transform infrared spectroscopy measurements reveal that the crystalline grains consist of highly crystalline pure hydroxyapatite phases. Transmission electron microscopy results show that rod-like hydroxyapatite-calcium grains with an average diameter of about 100 nm long and about 20 nm wide are uniformly distributed, which are also observed with an average pore size of 2-3 nm. Based on N{sub 2} adsorption-desorption isotherms investigation, the pore size, surface area and pore volume of mesoporous hydroxyapatite-calcium are 2.73 nm, 42.43 m{sup 2} g{sup -1} and 0.12 cm{sup 3} g{sup -1}, respectively.