Synthesis and characterization of α-MoO3 nanobelt composite positive electrode materials for lithium battery application

Graphical abstract: (a) TEM image of MoO{sub 3}/PEO nanobelts composite, (b) CV curves of MoO{sub 3}/PEO nanobelts composite. - Highlights: • α-MoO{sub 3} and PEO surfactant MoO{sub 3} nanobelts were synthesized by solvothermal method. • The capacity retention of 12.5 wt% PEO surfactant MoO{sub 3} nanobelts is 88.78%. • The specific capacity of 12.5 wt% PEO surfactant MoO{sub 3} nanobelts is 352 mAh g{sup −1}. • MoO{sub 3}/PEO nanobelts composite material demonstrates good cycling stability as cathode. - Abstract: α-MoO{sub 3} and PEO surfactant MoO{sub 3} nanobelts were synthesized by a solvothermal method. The morphology and nanostructure of samples were characterized by X-ray diffraction (XRD), Fourier transform infrared spectroscopy (FTIR), Raman spectroscopy, scanning electron microscopy (SEM) and transmission electron microscopy (TEM). Bare α-MoO{sub 3} and 12.5 wt% PEO surfactant MoO{sub 3} nanobelts have an initial specific capacities of 279 and 352 mAh g{sup −1}, respectively, at constant current density 30 mA g{sup −1} with potential range of 1.5–4.0 V vs. Li/Li{sup +}. While MoO{sub 3} is modified by the intercalation of PEO, it is effectively shielded against electrostatic interaction between the MoO{sub 3} interlayer and Li{sup +} ions. We reported positive material, a nanocomposite of MoO{sub 3} coated with polyethylenemore » oxide. It presents good cycling stability due to existence of the conductive and protective polyethylene oxide coating and the nanobelt morphology of MoO{sub 3}. The polyethylene oxide acts as a conducting matrix, a binder and an active material, as well as a volume change buffer agent, which holds the MoO{sub 3} particles in place during the discharge cycles. The cyclic voltammograms of the 12.5 wt% PEO surfactant MoO{sub 3} nanobelt composite displayed better cyclic performance compared with pure MoO{sub 3} nanobelts. The specific capacity of the pure MoO{sub 3} nanobelts and 12.5 wt% PEO surfactant MoO{sub 3} nanobelts exhibit as 199 mAh g{sup −1} and 225 mAh g{sup −1}, respectively, after 9 cycles, suggesting that the stability of surfactant material is worthy.« less