Meso/macroporous γ-Al2O3 fabricated by thermal decomposition of nanorods ammonium aluminium carbonate hydroxide

A B S T R A C T Through exploring the reaction parameters during the synthesis of the AACH, rod-like ammonium aluminium carbonate hydroxide (AACH) with high crystallinity has been successfully prepared via a facile hydrothermal method. The synthesis parameters like time, the molar ratio of NH4HCO3/Al and the properties of starting materials were systematically investigated. The structure was characterized using X-ray powder diffraction (XRD), scanning electron microscopy (SEM), IR and transmission electron microscopy (TEM). The experimental results display that the obtained g-Al2O3 materials possess meso/ macroporosity and large pore volume, which are mainly attributed to the removal of gas molecules during the decomposition of AACH. Moreover, using the rod-like AACH as precursor, g-Al2O3 nanorods were obtained via a low-temperature thermal decomposition method.