A cost-effective process to prepare VO2 (M) powder and films with superior thermochromic properties

Abstract VO 2 powder with superior phase transition performance was prepared by convenient thermolysis method. The results illustrated that VO 2 powder show high purity and crystallinity. VO 2 particles are transformed from cluster to quasi-sphere with the increase of annealing temperature. The DSC analysis proves that VO 2 show superior phase transition performance around 68 °C. The phase transition temperature can be reduced to 33.5 °C by 1.8 at% tungsten doping. The maximum decreasing efficiency of phase transition temperature is about −30 K/at% with w = 0.4 at%. After mixing VO 2 powder with acrylic resin, the maximal visible transmission of the composite thin films on glass is 48% and the transmission modulation at 2000 nm is 37.3% with phase transition temperature of 66.2 °C. Though the phase transition performance is weakened by tungsten doping, the film prepared by 1.3 at% tungsten doped VO 2 still show superior transmission modulation about 26.4% at 2000 nm, which means that it is a potential candidate as smart windows.