White light emission and energy transfer in Dy3+/Eu3+ co-doped BaLa2WO7 phosphors

Highlights: • BaLa{sub 2}WO{sub 7}:Dy{sup 3+}, Eu{sup 3+} phosphors were synthesized by solid-state reaction. • Eu{sup 3+} compensated the red emission component of the BaLa{sub 2}WO{sub 7}:Dy{sup 3+} phosphor. • The observed emission lifetimes indicates the energy transfer from Dy{sup 3+} to Eu{sup 3+}. • BaLa{sub 2}WO{sub 7}:Dy{sup 3+}, Eu{sup 3+} are potential phosphors used in n-UV pumped white LEDs. - Abstract: Tunable full color emissive BaLa{sub 1.75−x}WO{sub 7}:0.25Dy{sup 3+}, xEu{sup 3+} phosphors which peaked at 484 nm (blue), 572 nm (yellow), 593 nm (orange), and 617 nm (red) were synthesized by the traditional solid-state reaction method. The as-synthesized phosphors were characterized by X-ray power diffraction, diffused reflectance spectra, photoluminescence decay curves, photoluminescence excitation and emission spectra. The photoluminescence excitation spectra range from 200 to 500 nm, including an O{sup 2−}⟶W{sup 6+} charge transfer band and several 4f–4f transition peaks of Dy{sup 3+} and Eu{sup 3+}. Co-doping with Eu{sup 3+} compensated the red emission component of the BaLa{sub 2}WO{sub 7}:Dy{sup 3+} phosphor. Furthermore, the energy transfer from Dy{sup 3+} to Eu{sup 3+} was confirmed based on the luminescence spectra and decay curves. The intense white light emissions are suggestive exploration for the potential phosphor for optical materials applications used inmore » the ultraviolet excited white light emitting diodes.« less