Hydrothermal synthesis of calcium-deficient hydroxyapatite whiskers and their thermal transformation to polycrystalline β-tricalcium phosphate short fibers
Source abstract
Abstract
Resorbable calcium phosphate fibers are of particular interest to reinforce biodegradable bone substitutes for load-bearing applications. The aim of the present study was to prepare calcium-deficient hydroxyapatite (dHAp) whiskers with a molar Ca/P ratio of 1·5 by a hydrothermal synthesis and to transform them to β-tricalcium phosphate (β-TCP) by a subsequent thermal treatment. For the hydrothermal synthesis, calcium tripolyphosphate was used and different amounts of 2-propanol were added to adjust the pH. Average whisker lengths of 160 µm were obtained at a 2-propanol content of 27 volume-percent. However, 33% dicalcium phosphate anhydrate (DCPA) were present as a secondary phase. The amount of DCPA could be reduced by increasing the amount of 2-propanol. Whisker samples consisting of 88% dHAp and 12% DCPA were selected to investigate microstructural changes and phase transformations during thermal treatment. Polycrystalline single phase -TCP short fibers were obtained after a thermal treatment at 1125°C.
Source: crossref · Quality: baseline
Research context
OpenAlex topics: Bone Tissue Engineering Materials · Dental materials and restorations · Additive Manufacturing and 3D Printing Technologies
SciVX discovery tags are terminology-based. OpenAlex topics are source-provided classifications.
Affiliations
Institute of Materials Science and Technology (IMT), Friedrich-Schiller-University of Jena, Jena, Germany
Department for Functional Materials in Medicine and Dentistry, University of Würzburg, Würzburg, Germany
References (34)
Show source-provided references
1. 10.1016/0142-9612(94)90263-110.1016/0142-9612(94)90263-1 ↗
2. 10.1557/JMR.1998.001510.1557/JMR.1998.0015 ↗
3. 10.1023/A:102058580057210.1023/A:1020585800572 ↗
4. 10.1016/0142-9612(80)90059-910.1016/0142-9612(80)90059-9 ↗
5. 10.1111/j.1551-2916.2007.01967.x10.1111/j.1551-2916.2007.01967.x ↗
6. 10.1111/j.1151-2916.1997.tb03197.x10.1111/j.1151-2916.1997.tb03197.x ↗
7. 10.1111/j.1151-2916.2001.tb00653.x10.1111/j.1151-2916.2001.tb00653.x ↗
8. 10.1016/j.matchemphys.2004.10.04910.1016/j.matchemphys.2004.10.049 ↗
9. 10.1016/S0272-8842(02)00153-010.1016/S0272-8842(02)00153-0 ↗
10. 10.1007/s10853-007-2032-910.1007/s10853-007-2032-9 ↗
11. 10.1557/JMR.1995.052110.1557/JMR.1995.0521 ↗
12. 10.1007/s10853-007-1853-x10.1007/s10853-007-1853-x ↗
13. 10.1021/cg800738a10.1021/cg800738a ↗
14. 10.1016/S0025-5408(99)00044-610.1016/S0025-5408(99)00044-6 ↗
15. 10.1016/S0277-5387(00)83673-610.1016/S0277-5387(00)83673-6 ↗
16. 10.1016/j.actbio.2010.02.01110.1016/j.actbio.2010.02.011 ↗
17. Roeder R. K. · Journal of the American Ceramic Society · 2006 · 89 · 209610.1111/j.1551-2916.2006.01067.x ↗
18. 10.1007/BF0035203910.1007/BF00352039 ↗
19. 10.1111/j.1551-2916.2008.02600.x10.1111/j.1551-2916.2008.02600.x ↗
20. 10.4131/jshpreview.7.139810.4131/jshpreview.7.1398 ↗
21. 10.2109/jcersj2.117.75910.2109/jcersj2.117.759 ↗
22. Mizutani Y. · British Ceramic Transactions · 1998 · 97 · 105
23. 10.1016/j.jeurceramsoc.2004.07.02810.1016/j.jeurceramsoc.2004.07.028 ↗
24. 10.1016/j.materresbull.2006.09.01510.1016/j.materresbull.2006.09.015 ↗
25. 10.1002/jbm.82027010510.1002/jbm.820270105 ↗
26. 10.1016/j.biomaterials.2008.03.02810.1016/j.biomaterials.2008.03.028 ↗
27. 10.1039/jr961000444210.1039/jr9610004442 ↗
28. 10.1007/BF0219621410.1007/BF02196214 ↗
29. 10.1016/j.jcat.2011.03.01410.1016/j.jcat.2011.03.014 ↗
30. 10.1016/0003-9969(66)90154-310.1016/0003-9969(66)90154-3 ↗
31. 10.1016/j.jssc.2005.08.00310.1016/j.jssc.2005.08.003 ↗
32. 10.1016/S0142-9612(98)00040-410.1016/S0142-9612(98)00040-4 ↗
33. 10.1023/A:101851242868310.1023/A:1018512428683 ↗
34. 10.1016/j.jeurceramsoc.2006.09.00510.1016/j.jeurceramsoc.2006.09.005 ↗