Polyphenylenesulfied/montomorillonite clay nanocomposite coatings: Their efficacy in protecting steel against corrosion

Nanoscale montomorillonite (MMT) clay fillers became dispersed in a polyphenylenesulfied (PPS) matrix through the processes of octadecylamine (ODA) intercalation {yields} molten PPS co-intercalation {yields} exfoliation. Cooling this molten exfoliated material led to the formation of a PPS/MMT nanocomposite. The MMT nanofiller conferred three advanced properties on the semi-crystalline PPS: First, it raised its melting point by nearly 40 C to 290 C; second, it increased its crystallization energy, implying that an excellent adherence of the nanofillers surfaces to PPS in terms of a good interfacial bond; and, third, it abated the degree of its hydrothermal oxidation due to sulfide {yields} sulfite linkage transformations. When this advanced PPS nanocomposite was used as a corrosion-preventing coating for carbon steel in a simulated geothermal environment at 300 C, a coating of {approx}150 {micro}m thickness adequately protected the steel against hot brine-caused corrosion. In contrast, an MMT-free PPS coating of similar thickness was not nearly as effective in mitigating corrosion as was the nanocompsite; in fact, the uptake of corrosive ionic electrolyte by the unmodified coating increased with an extending exposure time.