Microstructure and mechanical properties of partial transient liquid phase bonded Si3N4–DZ483 superalloy joints

Abstract Partial transient liquid phase bonding (PTLPB) was applied to silicon nitride/nickel-based superalloy (DZ483) joints using Ti/Cu/Ni interlayers. Microstructure examination and mechanical properties evaluation of the joints show that bonding of Si 3 N 4 to superalloy was successful. A uniform compact reaction layer about 2.7 μm thickness was found at the Si 3 N 4 /Ti interface, which was formed by the reaction between Ti and Si 3 N 4 substrate. With joining temperature rising, the flexural strength of the joining samples increased initially and then decreased. When the joining temperature was 1323 K, the flexural strength of the joints reached to 170 MPa. The fracture behavior of the joints was also discussed, with the ceramic reaction layer being the region where all failures occurred.