Effect of rare earth additions on the critical resolved shear stresses of magnesium alloys

An inverse optimization strategy based on crystal plasticity finite element simulations of polycrystals was used to obtain the critical resolved shear stresses of two Mg?1%Mn alloys containing neodymium from macroscopic experimental data. It was found that, with respect to pure Mg, the presence of Nd increases the CRSSbasal, CRSStwinning, and the CRSSbasal/CRSStwinning ratio and decreases the CRSSnon-basal/CRSStwinning ratio. Additions of neodymium as high as 1 wt% result in similar CRSSs values for all deformation modes and, thus, in an isotropic yielding behavior.