Synthesis of highly efficient MnOx catalyst for low-temperature NH3-SCR prepared from Mn-MOF-74 template

Abstract Spherical mesoporous MnO x nanoparticles were prepared by the thermolysis of a Mn-MOF-74 template. The morphologies of the MnO x nanoparticles were inherited from the Mn-MOF-74 template and the crystal structures of the MnO x particles could be regulated by changing the thermolysis conditions. These porous MnO x nanoparticles were tested as low-temperature selective catalytic reduction (SCR) catalysts and they exhibited high activities. The sample prepared at 700 °C under a N 2 atmosphere had the largest specific surface area (89.1 m 2 /g) and the highest deNO x activity (98% NO conversion) with a N 2 selectivity of almost 100%.