J-integral for spallation of protective layer subjected to metal dusting corrosion
Source abstract
Abstract
Abstract The failure of high temperature alloys exposed to a carburizing gas atmosphere due to metal dusting corrosion was studied. A coupled model of the solid subjected to mechano-diffusional stresses was developed. For an interface crack between the protective film and the alloy substrate under an applied diffusion stress, the J -integral for film spallation was determined. The effects of interface crack length, film thickness and film mechanical properties on the J -integral (that is, the energy release rate) for spallation were investigated. Finally, comparisons of calculated J -integral values and experimental results are given and discussed.
Source: openaire · Quality: candidate unverified · Source record ↗
Research context
OpenAlex topics: Fatigue and fracture mechanics · Numerical methods in engineering · Nuclear Materials and Properties
SciVX discovery tags are terminology-based. OpenAlex topics are source-provided classifications.
References (51)
Show source-provided references
1. Recent advances in understanding metal dusting: a review10.1002/maco.201005675 ↗
2. Metal dusting10.1002/maco.200303729 ↗
3. Metal dusting protective coating. A literature review10.1007/s11085-011-9248-4 ↗
4. Operational experience with diffusion coatings on steam cracker tubes10.1002/(SICI)1521-4176(199912)50:12<700::AID-MACO700>3.0.CO;2-0 ↗
5. Development of a metal dusting resistant functional coating by Sn and Al pack cementation10.1016/j.surfcoat.2016.04.067 ↗
6. Protective behaviour of newly developed coatings against metal dusting10.1002/maco.200303736 ↗
7. Microstructures, properties and high-temperature carburization resistances of HVOF thermal sprayed NiAl intermetallic-based alloy coatings10.1016/j.surfcoat.2003.08.080 ↗
8. Evolution of PVD Al oxide coatings in carburizing atmospheres at high temperature10.1016/j.surfcoat.2015.07.063 ↗
9. Prevention of metal dusting on Ni-based alloys by MCrAlY coatings10.1016/j.corsci.2007.04.002 ↗
10. Effect of pre-oxidation on coke formation and metal dusting of electroplated Ni3Al-CeO2-based coatings in CO-H2-H2O10.1002/maco.200804077 ↗
11. Protective coating against metal dusting10.1016/j.surfcoat.2008.09.023 ↗
12. Behavior of uncoated and coated pure Fe in metal dusting conditions10.1016/j.surfcoat.2016.08.095 ↗
13. Production, characterization and evaluation of protective Cr oxide coatings against metal dusting10.1016/j.surfcoat.2009.09.058 ↗
14. Initiation of metal-dusting pits and a method to mitigate metal-dusting corrosion10.1007/s11085-006-9032-z ↗
15. Control of metal dusting corrosion in Ni-based alloys10.1016/j.ijhydene.2006.08.050 ↗
16. Linear theory of thermochemical equilibrium of solids under stress10.1016/0001-6160(73)90021-7 ↗
17. Thermochemical equilibrium of multiphase solids under stress10.1016/0001-6160(78)90067-6 ↗
18. The effect of self-stress on diffusion in solids10.1016/0001-6160(82)90023-2 ↗
19. Phase-changes in a thin plate with nonlocal self-stress effects10.1016/0956-7151(92)90071-L ↗
20. Coupled hydrogen diffusion simulation using a heat transfer analogy10.1016/j.ijmecsci.2016.07.020 ↗
21. Numerical modeling of hydrogen diffusion in metals accounting for large deformations10.1016/j.ijhydene.2015.04.081 ↗
22. Prediction of crack propagation under cyclic loading based on hydrogen diffusion10.1016/j.matlet.2015.03.045 ↗
23. Prediction of diffusion assisted hydrogen embrittlement failure in high strength martensitic steels10.1016/j.jmps.2015.08.010 ↗
24. FE analysis of hydrogen diffusion around a crack tip in an austenitic stainless steel10.1016/j.ijhydene.2016.03.003 ↗
25. Two-dimensional chemo-elasticity under chemical equilibrium10.1016/j.ijsolstr.2014.11.025 ↗
26. Computational electro-chemo-mechanics of lithium-ion battery electrodes at finite strains10.1007/s00466-014-1102-5 ↗
27. Cyclic plasticity and shakedown in high-capacity electrodes of lithium-ion batteries10.1016/j.ijsolstr.2012.12.019 ↗
28. Size-dependent fracture of Si nanowire battery anodes10.1016/j.jmps.2011.06.003 ↗
29. Fracture of crystalline silicon nanopillars during electrochemical lithium insertion10.1073/pnas.1201088109 ↗
30. Modelling the coupling between hydrogen diffusion and the mechanical behaviour of metals10.1016/j.commatsci.2016.05.030 ↗
31. Stresses from oxide film imperfections during metal dusting10.1007/s11085-012-9307-5 ↗
32. Coupled mechano-diffusional driving forces for fracture in electrode materials10.1016/j.jpowsour.2012.12.034 ↗
33. Interface crack between two elastic layers10.1007/BF00018123 ↗
34. The role of T-stress on kinking angle of interface cracks10.1016/j.matdes.2015.05.007 ↗
35. Modeling of progressive delamination in a thin film drive by diffusion-induced stresses10.1016/j.ijsolstr.2013.04.003 ↗
36. Solute segregation and stress intensity factors at the edge of elastic thin-film electrodes under chemical equilibrium10.1016/j.jpowsour.2015.04.096 ↗
37. A path-independent integral for fracture of solids under combined electrochemical and mechanical loadings10.1016/j.jmps.2014.06.007 ↗
38. Helmut · 2007
39. Timoshenko · 2004
40. A path independent integral and the approximate analysis of strain concentration by notches and cracks10.1115/1.3601206 ↗
41. Crack propagation in continuous media10.1016/0021-8928(67)90034-2 ↗
42. On the J-integral for bi-material bodies10.1007/BF00040155 ↗
43. Analysis of interface cracks dissimilar isotropic materials using conservation integrals in elasticity10.1016/0013-7944(84)90048-1 ↗
44. On the path independent integral-J10.1016/0013-7944(80)90015-6 ↗
45. The energy release rate for hygrothermal coupling elastic materials10.1007/s10409-006-0087-5 ↗
46. Partial molar volumes from high-temperature lattice parameters of iron-carbon austenites10.1179/msc.1970.4.1.219 ↗
47. Molybdenum effect on Fe-Cr-Ni-alloy elastic constants10.1557/JMR.1988.0040 ↗
48. Determination and analysis of crack growth resistance in plasma-sprayed thermal barrier coatings10.1016/j.engfracmech.2010.02.007 ↗
49. Determining the critical strain energy release rate of plasma-sprayed coating using a double-cantilever-beam technique10.1111/j.1151-2916.1988.tb07542.x ↗
50. Mechanism governing the performance of thermal barrier coatings10.1016/S1359-0286(99)00024-8 ↗
51. In situ measurement of the toughness of the interface between a thermal barrier coating and a Ni alloy10.1111/j.1551-2916.2011.04588.x ↗