Composite cerium oxide/titanium oxide thin films for corrosion protection of AZ91D magnesium alloy via sol–gel process

Abstract Anti‐corrosive composite cerium oxide/titanium oxide (CeO₂/TiO₂) thin films were successfully prepared on an AZ91D magnesium alloy substrate by applying cerium oxide (CeO₂) thin films as the inner layer with a sol–gel process. Composition and surface morphology of the thin films were analyzed using X‐ray diffraction (XRD) and scanning electron microscope (SEM). XRD showed that the composite films consisted of cerianite and anatase phases. The wettability of the thin films was evaluated by water contact angles measurements. Potentiodynamic polarization curves and electrochemical impedance spectroscopy (EIS) tests were used to evaluate the corrosion behavior of the bare substrate and coated samples in 3.5 wt% sodium chloride solution (3.5 wt% NaCl). The results demonstrated that titanium oxide (TiO₂) thin film mainly dominated the corrosion resistance of samples and the composite films with excellent hydrophilicity could significantly improve the corrosion resistance of AZ91D magnesium alloy.