Effect of graphene on the electrochemical protection of zinc‐rich coatings
Source abstract
Abstract
The effect of graphene on electrochemical protection of zinc‐rich coatings was studied by electrochemical impedance spectroscopy (EIS) and the monitoring of open circuit potential (OCP) versus time of immersion. The obtained results show that addition of 2.5 wt% graphene to zinc‐rich coating prolongs the lifetime of cathodic protection to mild steel immersion in sodium chloride solution. On the basis of these consistent finds, two protective mechanisms of graphene are assumed. On the one hand, the embedded graphene could serve as electrical conduction paths between zinc particles. On the other hand, the more distributed graphene may lead to the galvanic corrosion of mild steel.
Source: crossref · Quality: baseline
Research context
OpenAlex topics: Corrosion Behavior and Inhibition · Non-Destructive Testing Techniques · Concrete Corrosion and Durability
SciVX discovery tags are terminology-based. OpenAlex topics are source-provided classifications.
Affiliations
College of Chemistry and Pharmaceutical Sciences Qingdao Agricultural University 700 Changcheng Road Qingdao 266109 P.R. China
Funding
Natural Science Foundation of Shandong Province
References (41)
Show source-provided references
1. 10.1007/BF0063803910.1007/BF00638039 ↗
2. 10.5006/1.331594810.5006/1.3315948 ↗
3. 10.1016/0010-938X(74)90001-810.1016/0010-938X(74)90001-8 ↗
4. 10.1016/j.porgcoat.2005.06.00910.1016/j.porgcoat.2005.06.009 ↗
5. 10.1016/j.electacta.2010.04.01810.1016/j.electacta.2010.04.018 ↗
6. 10.1016/j.corsci.2016.03.02310.1016/j.corsci.2016.03.023 ↗
7. 10.1016/0010-938X(94)90002-710.1016/0010-938X(94)90002-7 ↗
8. 10.1016/j.corsci.2012.10.00410.1016/j.corsci.2012.10.004 ↗
9. 10.1016/j.porgcoat.2006.08.01510.1016/j.porgcoat.2006.08.015 ↗
10. 10.1016/j.porgcoat.2013.11.00410.1016/j.porgcoat.2013.11.004 ↗
11. 10.1016/j.apsusc.2014.12.03410.1016/j.apsusc.2014.12.034 ↗
12. 10.1016/j.electacta.2003.11.03110.1016/j.electacta.2003.11.031 ↗
13. 10.1016/j.electacta.2007.09.05610.1016/j.electacta.2007.09.056 ↗
14. 10.1038/nmat184910.1038/nmat1849 ↗
15. 10.1021/cm504309910.1021/cm5043099 ↗
16. 10.1021/acsami.5b0553110.1021/acsami.5b05531 ↗
17. 10.1179/1743278214Y.000000023210.1179/1743278214Y.0000000232 ↗
18. 10.1166/nnl.2015.204310.1166/nnl.2015.2043 ↗
19. 10.1016/j.surfcoat.2015.03.04610.1016/j.surfcoat.2015.03.046 ↗
20. 10.1016/j.carbon.2014.10.03710.1016/j.carbon.2014.10.037 ↗
21. 10.1007/s12043-015-1005-910.1007/s12043-015-1005-9 ↗
22. 10.1016/j.porgcoat.2015.05.00110.1016/j.porgcoat.2015.05.001 ↗
23. 10.1016/j.porgcoat.2015.07.00510.1016/j.porgcoat.2015.07.005 ↗
24. 10.1016/j.surfcoat.2015.06.02710.1016/j.surfcoat.2015.06.027 ↗
25. 10.1016/j.apsusc.2015.06.02610.1016/j.apsusc.2015.06.026 ↗
26. 10.3390/ijms1601223910.3390/ijms16012239 ↗
27. 10.1016/j.corsci.2016.11.00910.1016/j.corsci.2016.11.009 ↗
28. 10.1016/j.carbon.2016.12.04410.1016/j.carbon.2016.12.044 ↗
29. 10.1016/j.cej.2016.06.02810.1016/j.cej.2016.06.028 ↗
30. 10.1016/j.surfcoat.2015.12.05610.1016/j.surfcoat.2015.12.056 ↗
31. 10.1021/nn203507y10.1021/nn203507y ↗
32. 10.1021/cm100477v10.1021/cm100477v ↗
33. 10.1021/nn900020u10.1021/nn900020u ↗
34. 10.1002/adma.20080075710.1002/adma.200800757 ↗
35. 10.1021/nn401435610.1021/nn4014356 ↗
36. 10.1021/nn402150t10.1021/nn402150t ↗
37. 10.1103/PhysRevLett.97.18740110.1103/PhysRevLett.97.187401 ↗
38. 10.1038/nnano.2013.4610.1038/nnano.2013.46 ↗
39. 10.1021/ja200245p10.1021/ja200245p ↗
40. 10.1021/nn302784m10.1021/nn302784m ↗
41. 10.1016/0013-4686(96)00021-710.1016/0013-4686(96)00021-7 ↗