Yttrium Ion Release and Phase Transformation in Yttria-Stabilized Zirconia Under Acidic Conditions: Implications for Dental Implant Durability

The stability of yttria-stabilized zirconia (YSZ) as a dental implant material is highly dependent on its resistance to low-temperature degradation (LTD) and surface dissolution, particularly in acidic oral environments. This study investigates the effects of yttrium ion (Y3+) release on the phase stability of zirconia during constant immersion and pH cycling tests, simulating oral conditions. Zirconia disks were immersed in acidic (pH 2), neutral (pH 7), and basic (pH 10) solutions over a 27-day period. Inductively coupled plasma (ICP) analysis revealed significant yttrium ion release during acidic phases, while zirconium ion (Zr4+) release remained minimal. X-ray photoelectron spectroscopy (XPS) showed a shift in zirconium 3d binding energies, indicating a transformation from the tetragonal to the monoclinic phase, driven by yttrium leaching. X-ray diffraction (XRD) confirmed this phase change, with the appearance of the monoclinic (111) peak after exposure to acidic conditions. This study concludes that yttrium ion depletion under acidic conditions destabilizes the tetragonal phase, promoting LTD and compromising the material’s long-term performance as a dental implant or restorative material.