Influence of Boehmite Nanoparticle Loading on the Mechanical, Thermal, and Rheological Properties of Biodegradable Polylactide/Poly(ϵ‐caprolactone) Blends
Source abstract
Abstract
Abstract Blends of polylactide (PLA) and poly(ϵ‐caprolactone) (PCL) were melt‐processed with boehmite (BAI) nanoparticles to produce ternary biocomposites with the intent of broadening the potential applications of PLA. The mechanical properties of the prepared composites exhibited remarkable improvement in the elongation‐at‐break of between 60 and 430% for increasing loadings of PCL and BAI in the blends. Furthermore, the melting temperatures of PLA and PCL were observed to shift approximately 2 °C toward each other in the composites, an indication of improved compatibility. This partial compatibility was also observed from the electron microscopy images, which also revealed a good dispersion of PCL in the PLA. The composite with balanced properties was found to be consisting of 70 wt% PLA, 30 wt% PCL, and 4 wt% BAI.
Source: crossref · Quality: baseline
Research context
OpenAlex topics: biodegradable polymer synthesis and properties · Natural Fiber Reinforced Composites · Electrospun Nanofibers in Biomedical Applications
SciVX discovery tags are terminology-based. OpenAlex topics are source-provided classifications.
Affiliations
DST/CSIR National Centre for Nanostructured Materials Council for Scientific and Industrial Research Pretoria 0001 South Africa
Division of Polymer Technology, Department of Chemical, Metallurgical Material Engineering, Tshwane University of Technology Pretoria 0001 South Africa
Department of Applied Chemistry University of Johannesburg Doornfontein 2028 Johannesburg South Africa
References (65)
Show source-provided references
1. 10.1016/j.wasman.2010.10.02910.1016/j.wasman.2010.10.029 ↗
2. 10.1016/j.compositesa.2011.01.01710.1016/j.compositesa.2011.01.017 ↗
3. 10.3390/ma202030710.3390/ma2020307 ↗
4. Xiao L. · 2012 · 247
5. 10.1016/j.polymdegradstab.2009.12.01910.1016/j.polymdegradstab.2009.12.019 ↗
6. 10.1016/j.eurpolymj.2012.12.00810.1016/j.eurpolymj.2012.12.008 ↗
7. 10.2174/09298671179834732410.2174/092986711798347324 ↗
8. 10.1016/j.foodres.2013.01.05010.1016/j.foodres.2013.01.050 ↗
9. 10.1016/j.msec.2008.08.00210.1016/j.msec.2008.08.002 ↗
10. 10.1021/ar300037610.1021/ar3000376 ↗
11. 10.1016/j.polymdegradstab.2013.01.00510.1016/j.polymdegradstab.2013.01.005 ↗
12. 10.1016/j.indcrop.2007.01.00310.1016/j.indcrop.2007.01.003 ↗
13. 10.1016/j.polymdegradstab.2010.07.01610.1016/j.polymdegradstab.2010.07.016 ↗
14. 10.1016/j.jmbbm.2010.12.00610.1016/j.jmbbm.2010.12.006 ↗
15. 10.1016/j.arabjc.2010.08.00310.1016/j.arabjc.2010.08.003 ↗
16. 10.1016/j.engfracmech.2011.09.01010.1016/j.engfracmech.2011.09.010 ↗
17. 10.1021/am201850m10.1021/am201850m ↗
18. 10.1021/am301842e10.1021/am301842e ↗
19. 10.1016/j.eurpolymj.2009.04.02810.1016/j.eurpolymj.2009.04.028 ↗
20. 10.1016/j.jiec.2011.11.15310.1016/j.jiec.2011.11.153 ↗
21. 10.1021/ma202505f10.1021/ma202505f ↗
22. 10.1016/j.jmbbm.2007.12.00110.1016/j.jmbbm.2007.12.001 ↗
23. 10.1016/j.eurpolymj.2011.10.00910.1016/j.eurpolymj.2011.10.009 ↗
24. 10.1016/j.jmbbm.2010.10.00310.1016/j.jmbbm.2010.10.003 ↗
25. 10.1016/j.carbpol.2007.05.04010.1016/j.carbpol.2007.05.040 ↗
26. 10.1002/app.1113410.1002/app.11134 ↗
27. 10.1016/j.actbio.2009.07.01210.1016/j.actbio.2009.07.012 ↗
28. 10.1016/j.biomaterials.2010.09.07310.1016/j.biomaterials.2010.09.073 ↗
29. 10.1016/j.carbpol.2010.06.01210.1016/j.carbpol.2010.06.012 ↗
30. 10.1016/j.egypro.2013.06.78310.1016/j.egypro.2013.06.783 ↗
31. 10.1021/bm801183f10.1021/bm801183f ↗
32. 10.3139/978344643650310.3139/9783446436503 ↗
33. 10.1021/ie400430510.1021/ie4004305 ↗
34. 10.1016/j.polymertesting.2013.02.00810.1016/j.polymertesting.2013.02.008 ↗
35. 10.1002/mame.20080014610.1002/mame.200800146 ↗
36. 10.1016/j.polymer.2004.10.00910.1016/j.polymer.2004.10.009 ↗
37. Lipatov Y. S. · 1995
38. 10.1103/PhysRevLett.82.402610.1103/PhysRevLett.82.4026 ↗
39. 10.1002/mame.20110014810.1002/mame.201100148 ↗
40. 10.1002/mame.20110025410.1002/mame.201100254 ↗
41. 10.1007/s10853-010-4882-910.1007/s10853-010-4882-9 ↗
42. 10.1002/mame.20070035410.1002/mame.200700354 ↗
43. 10.1002/mame.20080036010.1002/mame.200800360 ↗
44. 10.1016/j.polymer.2004.05.02910.1016/j.polymer.2004.05.029 ↗
45. 10.1016/j.polymdegradstab.2010.04.00110.1016/j.polymdegradstab.2010.04.001 ↗
46. 10.1016/j.msea.2009.03.00310.1016/j.msea.2009.03.003 ↗
47. 10.1016/j.eurpolymj.2012.12.00610.1016/j.eurpolymj.2012.12.006 ↗
48. 10.1002/app.2980010.1002/app.29800 ↗
49. 10.1016/j.polymer.2011.11.06310.1016/j.polymer.2011.11.063 ↗
50. 10.1002/pen.2196810.1002/pen.21968 ↗
51. 10.3144/expresspolymlett.2011.8410.3144/expresspolymlett.2011.84 ↗
52. 10.1021/ma020237a10.1021/ma020237a ↗
53. 10.1016/j.carbpol.2011.05.04410.1016/j.carbpol.2011.05.044 ↗
54. 10.1021/am400482f10.1021/am400482f ↗
55. 10.1016/j.eurpolymj.2008.04.02310.1016/j.eurpolymj.2008.04.023 ↗
56. 10.1016/j.compositesa.2011.07.00310.1016/j.compositesa.2011.07.003 ↗
57. 10.1016/j.polymer.2011.12.00710.1016/j.polymer.2011.12.007 ↗
58. 10.1016/j.polymdegradstab.2012.11.01610.1016/j.polymdegradstab.2012.11.016 ↗
59. 10.1021/jp911198p10.1021/jp911198p ↗
60. 10.1155/2013/95169610.1155/2013/951696 ↗
61. 10.1016/j.procir.2013.01.02210.1016/j.procir.2013.01.022 ↗
62. 10.1016/j.polymer.2009.11.05810.1016/j.polymer.2009.11.058 ↗
63. 10.1021/ma021728y10.1021/ma021728y ↗
64. 10.1016/j.compositesa.2011.04.01210.1016/j.compositesa.2011.04.012 ↗
65. 10.1021/ma002191w10.1021/ma002191w ↗