Coupling Influence of pH and Cl– on the Corrosion Evolution of Passivated Q355B Steel in Simulated Concrete Pore Solution
Source abstract
Abstract
Electrochemical tests combined with surface characterization techniques were used to investigate the corrosion evolution of passivated Q355B steel under the dual action of pH and chloride. The results show that the Q355B passivation film in simulated concrete pore solution is the amorphous oxide layer, and pH and Cl – have closely coupled effects on Q355B corrosion. Meanwhile, the impact of pH is more significant: the decrease in pH shifts from pitting to uniform corrosion. Furthermore, we found that chloride-induced defects in the passivation film and the Cl – congregate phenomenon jointly controlled the pitting.
Source: openalex_inverted_index · Quality: baseline
Research context
OpenAlex topics: Concrete Corrosion and Durability · Corrosion Behavior and Inhibition · Hydrogen embrittlement and corrosion behaviors in metals
SciVX discovery tags are terminology-based. OpenAlex topics are source-provided classifications.
Affiliations
College of Materials Science and Engineering
Hohai University
Key Laboratory of Advanced Marine Materials, Ningbo Institute of Materials Technology and Engineering
Chinese Academy of Sciences
Funding
National Key Research and Development Program of China · Ningbo Municipal Bureau of Science and Technology · Chinese Academy of Sciences
References (70)
Show source-provided references
1. 10.1016/j.conbuildmat.2017.03.13210.1016/j.conbuildmat.2017.03.132 ↗
2. 10.1016/j.electacta.2009.07.01310.1016/j.electacta.2009.07.013 ↗
3. 10.1021/acsomega.3c0001310.1021/acsomega.3c00013 ↗
4. Koch G. H. · 2002
5. 10.1016/j.jobe.2024.10994510.1016/j.jobe.2024.109945 ↗
6. 10.1016/j.corsci.2022.11048210.1016/j.corsci.2022.110482 ↗
7. 10.1016/j.jobe.2023.10774210.1016/j.jobe.2023.107742 ↗
8. 10.1016/j.conbuildmat.2017.01.00710.1016/j.conbuildmat.2017.01.007 ↗
9. 10.1016/j.electacta.2011.02.09410.1016/j.electacta.2011.02.094 ↗
10. 10.1016/j.jelechem.2021.11545410.1016/j.jelechem.2021.115454 ↗
11. 10.1016/j.corsci.2008.06.04710.1016/j.corsci.2008.06.047 ↗
12. 10.1016/j.corsci.2009.02.02610.1016/j.corsci.2009.02.026 ↗
13. 10.1016/j.corsci.2012.05.02510.1016/j.corsci.2012.05.025 ↗
14. 10.1016/j.cemconres.2017.10.00710.1016/j.cemconres.2017.10.007 ↗
15. 10.1016/j.cemconres.2009.08.00610.1016/j.cemconres.2009.08.006 ↗
16. 10.1016/j.cemconres.2003.11.00910.1016/j.cemconres.2003.11.009 ↗
17. 10.1002/maco.20160931010.1002/maco.201609310 ↗
18. 10.1016/j.conbuildmat.2016.07.07810.1016/j.conbuildmat.2016.07.078 ↗
19. 10.1016/j.corsci.2007.05.00710.1016/j.corsci.2007.05.007 ↗
20. 10.1016/j.electacta.2011.04.12410.1016/j.electacta.2011.04.124 ↗
21. 10.1016/j.conbuildmat.2010.11.09910.1016/j.conbuildmat.2010.11.099 ↗
22. 10.1016/j.cemconres.2012.07.00410.1016/j.cemconres.2012.07.004 ↗
23. 10.1016/j.compstruct.2023.11667010.1016/j.compstruct.2023.116670 ↗
24. 10.1515/corrrev-2017-008810.1515/corrrev-2017-0088 ↗
25. 10.1016/j.jcsr.2005.09.00910.1016/j.jcsr.2005.09.009 ↗
26. 10.1016/j.engstruct.2020.11102710.1016/j.engstruct.2020.111027 ↗
27. 10.1016/j.engstruct.2022.11450710.1016/j.engstruct.2022.114507 ↗
28. 10.1016/j.cemconres.2004.06.00410.1016/j.cemconres.2004.06.004 ↗
29. 10.1016/j.conbuildmat.2023.13406010.1016/j.conbuildmat.2023.134060 ↗
30. 10.1016/j.conbuildmat.2020.11956410.1016/j.conbuildmat.2020.119564 ↗
31. 10.1016/j.corsci.2014.04.02310.1016/j.corsci.2014.04.023 ↗
32. Zhang P. · J. Wuhan Univ. Sci. Technol. · 2010 · 33 · 176
33. 10.1016/j.jobe.2022.10497810.1016/j.jobe.2022.104978 ↗
34. 10.3390/su1010381410.3390/su10103814 ↗
35. 10.1016/j.jmrt.2023.07.18010.1016/j.jmrt.2023.07.180 ↗
36. 10.1016/j.apsusc.2016.07.14210.1016/j.apsusc.2016.07.142 ↗
37. 10.1016/j.conbuildmat.2014.07.08210.1016/j.conbuildmat.2014.07.082 ↗
38. 10.1016/j.cemconcomp.2024.10580210.1016/j.cemconcomp.2024.105802 ↗
39. 10.1016/j.conbuildmat.2014.01.03010.1016/j.conbuildmat.2014.01.030 ↗
40. 10.1016/j.conbuildmat.2015.05.07310.1016/j.conbuildmat.2015.05.073 ↗
41. 10.1016/j.corsci.2012.01.01910.1016/j.corsci.2012.01.019 ↗
42. 10.1016/j.cemconcomp.2008.10.00310.1016/j.cemconcomp.2008.10.003 ↗
43. 10.1016/j.electacta.2012.12.12510.1016/j.electacta.2012.12.125 ↗
44. 10.1016/j.conbuildmat.2023.13475610.1016/j.conbuildmat.2023.134756 ↗
45. 10.1016/j.cemconcomp.2024.10543210.1016/j.cemconcomp.2024.105432 ↗
46. 10.1016/j.corsci.2020.10883010.1016/j.corsci.2020.108830 ↗
47. 10.1016/j.cemconcomp.2020.10353210.1016/j.cemconcomp.2020.103532 ↗
48. 10.1016/j.molstruc.2021.12990110.1016/j.molstruc.2021.129901 ↗
49. 10.1016/j.corsci.2018.01.04310.1016/j.corsci.2018.01.043 ↗
50. 10.1016/j.corsci.2020.10861010.1016/j.corsci.2020.108610 ↗
51. 10.1016/j.corsci.2022.11045110.1016/j.corsci.2022.110451 ↗
52. 10.1016/j.cemconcomp.2018.02.00210.1016/j.cemconcomp.2018.02.002 ↗
53. 10.1007/s10854-019-01055-z10.1007/s10854-019-01055-z ↗
54. 10.1016/j.conbuildmat.2016.02.04710.1016/j.conbuildmat.2016.02.047 ↗
55. 10.1016/j.ultsonch.2015.08.01810.1016/j.ultsonch.2015.08.018 ↗
56. 10.1016/0010-938X(94)00133-Q10.1016/0010-938X(94)00133-Q ↗
57. 10.1016/j.jmrt.2022.01.01810.1016/j.jmrt.2022.01.018 ↗
58. 10.1016/j.comptc.2016.12.00910.1016/j.comptc.2016.12.009 ↗
59. 10.1007/s10853-021-06542-510.1007/s10853-021-06542-5 ↗
60. 10.1016/S0958-9465(03)00037-410.1016/S0958-9465(03)00037-4 ↗
61. 10.1016/j.corsci.2010.12.03010.1016/j.corsci.2010.12.030 ↗
62. 10.1016/j.corsci.2021.10966910.1016/j.corsci.2021.109669 ↗
63. 10.20964/2020.07.4310.20964/2020.07.43 ↗
64. 10.1007/s10853-021-06237-x10.1007/s10853-021-06237-x ↗
65. 10.1016/S0958-9465(01)00022-110.1016/S0958-9465(01)00022-1 ↗
66. 10.1002/jrs.310910.1002/jrs.3109 ↗
67. 10.1016/j.conbuildmat.2024.13783910.1016/j.conbuildmat.2024.137839 ↗
68. 10.1016/j.corsci.2024.11196110.1016/j.corsci.2024.111961 ↗
69. 10.1016/j.conbuildmat.2020.11911610.1016/j.conbuildmat.2020.119116 ↗
70. 10.1016/j.jallcom.2018.07.02910.1016/j.jallcom.2018.07.029 ↗